鋼坯拉出 的英文怎麼說

中文拼音 [gāngpīlāchū]
鋼坯拉出 英文
withdrawal of section
  • 鋼 : 鋼名詞（鐵和碳的合金） steel
  • 坯 : 名詞1 （未經燒制的磚、瓦、瓷等的製品） base 2 （土坯） unburnt brick; earthen brick; adobe 3 [方...
  • 拉 : 拉構詞成分。
  • 拉出 : pull-out; exhaustion; unreeve; haul out; drag out拉出輥 pull-out rolls; 拉出器 puller
  1. Qualified molten steel from the steelmaking furnace will be contained in ladle and conveyed to continuous caster, poured into crastyllizer through pouring basket, then handled with the processes of vibration, water spraying cooling, straightening, roll conveying, flame cutting, and cooling on cooling bed, finally the formed billets will be stored at the stockyard or directly sent to the heating furnace of rolling mill for heating

    煉鋼爐冶煉出合格的鋼水，用鋼水包送至連鑄機，經中間包澆注到結晶器，再經振動水噴淋冷卻拉矯輥道輸送火焰切割冷床冷卻，最後存放于鋼坯堆放區或直接送至軋鋼機加熱爐進行加熱。
  2. According to numerical simulation and molten steel solidification mechanism, in the paper, the restrict relationship had been setup between casting speed and molten steel level and average mould tapping section thickness as well as its shell temperature at tapping spout

    本文基於數值模擬和鋼液凝固機理，建立起結晶器內鋼液液位和鑄坯拉速對其出鋼口處鋼液截面平均溫度和坯殼溫度的制約關系。
  3. Testing results are analyzed, then the boundary condition ( the heat transfer coefficient of and the water density ) for computer simulation is acquired. through simulation in computer using the all - purpose computer simulation software secondary cooling in slab continuous casting and test results, the influence of the factor such as casting speed, casting temperature, shell thickness and secondary cooling system are analyzed. the secondary cooling system is evaluated, the reasons of crack are analyzed

    應用模擬軟體和實驗數據對寶鋼1930鑄機進行了模擬計算，分析了拉速、配水制度、過熱度對鑄坯溫度場和坯殼厚度的影響；對寶鋼1930鑄機的二冷制度進行了評估，分析了產生裂紋的原因；並對二冷制度進行優化，提出了改進建議。
  4. Abstract : this article presents the problems and the reasons causing the problems in the operation of slab ccm mold in pansteel. a study has been carried out on the efficient ccm mold featuring high casting speed. and following the study relative technical measures are put forward, which ensure an increase of the ccm casting speed

    文摘:分析了攀鋼板坯連鑄結晶器在使用中出現的問題及其產生原因，對以高拉速為核心的高效連鑄結晶器結構進行了研究，提出了相應的技術措施，確保了攀鋼連鑄機拉速的提高。
  5. Abstract : according to the site condition of the bisc, a mathematical model of two - dimensional unsteady solidification and heat transfer was established for the bloom caster in the mold. the mathematical model was solved with a finite difference method to characterize the temperature profiles and thickness of the solidified shell in the mold, the effects of casting speed on thickness of the solidified shell are also studied

    文摘:根據包鋼的現場條件，建立了大方坯連鑄機結晶器內二維非穩態凝固傳熱數學模型，採用有限差分法對數學模型求解，得出結晶器中鑄坯的溫度分佈規律和凝固坯殼生成規律，同時研究了拉坯速度對坯殼生成厚度的影響