acrylate monomer 中文意思是什麼

acrylate monomer 解釋
丙烯酸酯單體
  1. In this thesis, the development of emulsion polymerization theory and related new technologies are comprehensively reviewed, and the synthetic technologies of acrylate latex modified by organosilicon both at home and abroad are also reviewed. based on the current development and research in this field, attentions of this study are focused on three ways for preparing novel acrylate latexes modified by organosilicons, that is, 1 ) the acrylate monomers are copolymerized with unsaturated silicons by emulsion copolymerization ; 2 ) a new latex with microphase separation morphology is synthesized, which shows a core - shell structure character ; 3 ) soap - free polymerization is explored for preparing a higher - performance latex using an unsaturated silicon monomer, different acrylates and a reactive emulsifier. by using techniques of delaying addition of organosilicon monomer and a hydrolysis inhibitor, the hydrolysis and condensation of 3 - ( trimethoxysilyl ) propyl methacrylate during polymerization can be effectively prevented, as a result, organosilicon content in the macromolecular chain is increased

    同時採用有機硅單體延遲滴加及添加水解抑制劑等技術，有效防止了-甲基丙烯酰氧基丙基三甲氧基硅烷在乳液聚合過程中的過渡水解及縮合反應，提高了聚合物大分子鏈中有機硅鏈節的含量；利用紅外光譜與差示掃描量熱儀對產物分子結構進行了表徵，並通過對共聚產物力學和吸水率的測試，證實了本研究所制備的有機硅改性丙烯酸酯共聚物具有比純丙烯酸酯聚合物更優良的力學及耐水性能；從分子設計角度出發，利用醇解反應合成出水解、縮合反應速率較慢的兩種新型不飽和有機硅單體： ?甲基丙烯酰氧基丙基三乙氧基硅烷和?甲基丙烯酰氧基丙基三異丙氧基硅烷；利用核磁共振對新型硅烷單體結構進行了證實；研究表明利用新型硅烷單體可以制備出高硅烷含量的有機硅改性丙烯酸酯乳液，且其聚合產物具有較高的力學及耐水性能。
  2. Butyl acrylate was selected as the tender monomer in prepared bpua, and when the viscosity of middle multipolymer is 800 - 1000mpa. s, the last prepolymer had good capability. in the applied research, some influencing factors such as diluent, photoinitiator and photoinitiators that match to different pigments on the coating film were studied

    根據研究的結果，進行大量的配方實驗，研製了適合於皮革使用的uv上光油，經性能測試顯示：光澤度110 、耐折性3萬次、耐溶劑性200次、附著力合格，達到皮革上光油的使用要求。
  3. Synthesis and photopolymerization kinetics study of propenyl ether - acrylate hybrid monomer

    丙烯酸酯雜化單體的合成及光聚合動力學研究
  4. Results show that self - crosslinkable latex at room temperature with high elasticity can be prepared when amount of butyl acrylate is 60 %, and amount of methyl methacrylate is 40 %, and mass ratio of nonionic emulsifier to anionic emulsifer is 3 : 1, and amount of initiator is 0. 6 %, and amount of self - crosslinkable monomer and protective colloid is 2 % and 0. 4 % respectively

    研究結果表明：當丙烯酸丁酯的質量為60 % ，甲基丙烯酸甲酯的質量為40 % ，非離子乳化劑和陰離子乳化劑的質量配比為3 : 1 ，引發劑的質量為0 . 6 % ，自交聯單體的質量為2 % ，保護膠體的質量為0 . 4 %時，可以制備出高彈性自交聯乳液。
  5. In this paper, interpenetrating polymer networks ( ipn ) based on polysiloxane ( pdms ) and poly ( methyl acrylate ) ( pma ) were prepared by using ma monomer and two types of pdms, which viscosities were 3300pa s and 7000pa s respectively. pdms was crosslmked by tetraethyl orthosilicate

    本論文制備了聚二甲基硅氧烷與聚丙烯酸甲酯的序列半互穿聚合物網路，其中聚硅氧烷為交聯結構，採用粘度分別為3300pa ? s和7000pa ? s兩個品種，聚丙烯酸甲酯為線性聚合物。
  6. In this paper, using partly neutralized acrylic as monomer and kaolin as abio - filler, poly ( sodium acrylate ) / kaolin composite superabsorbent was prepared and its properties were studied

    摘要以部分中和的丙烯酸為單體，以高嶺土為無機填充料，通過反相懸浮聚合法合成出聚丙烯酸鈉高嶺土復合高吸水性樹脂。
  7. Synthesis of polyacrylic acid emulsion containing hexafluorobutyl acrylate monomer ester and its use on cotton fabrics

    含丙烯酸六氟丁酯單體的丙烯酸酯共聚乳液的合成及其在棉織物上的應用