This paper deals with high fluid concrete in which high strength ceramsite made from shale was used as coarse aggregate. effects of cement content, water - cement ratio, sand percentage, mineral admixture, grading and pretreatment of lightweight aggregate on compressive strength and workability of high fluid structural lightweight aggregate concrete have been studied. the rules of water absorption of high strength lightweight aggregate under different pressure and effects on uniformity of high fluid structural lightweight aggregate concrete have been studied too
本文採用高強頁巖陶粒，摻加高效減水劑配製大流動性結構輕集料混凝土，討論了水泥用量、水灰比、砂率、礦物摻料及輕集料的級配和預濕方式對大流動性結構輕集料混凝土強度和工作性的影響；系統研究了高強陶粒在常壓和壓力下的吸水規律；研究了影響大流動性結構輕集料混凝土勻質性的因素，提出了解決大流動性結構輕集料混凝土分層離析的具體措施。 -
Based on above, the characteristics of hydration hardening process and microstructure of hsc as well as the interfacial layer between cement paste and coarse aggregate are investigated under low water cement ratio, high content superplasticiser and with one kind or more than one kind of mineral materials condition, the reaction mechanisms of different mineral materials are also discussed
研究了不同水膠比、復合緩凝成分高效減水劑及礦物摻合料的摻加方式、摻量對高強混凝土水泥漿體水化放熱過程和水泥漿體的水化熱、水化放熱速率以及最高溫升的影響規律。探明了高強混凝土中水泥漿體的水化硬化過程、礦物摻合料之間的相互作用機理。 -
Through much analysis of laboratory experiments, this paper reach the conclusion that aggregate gradation, degree of compaction, water cement ratio and magnitude of cement are the main factors that influence the coefficient of permeability and the compressive resilience modulus of high air void cement - stabilized crushed stone mixture
本文通過大量的室內試驗發現，集料級配組成、壓實度、水灰比和水泥用量是影響大孔隙水泥穩定碎石混合料滲透系數和抗壓回彈模量的主要因素。 -
Based on the basic principles of densified systems containing homogeneously arranged ultra - fine particles ( dsp ) and reactive powder concrete ( rpc ) adopted by foreign researchers specialized in building materials, silica rume, ultra - fine fly ash, quartz powder, 52. 5 - class portland cement and superplasticizer were selected and mixed, the theoretic of mixed steel fiber reinforced cement - based composite materials and of micro - aggregate filling voids were applied, the composition was adjusted, the mixture ratio of rpc was optimized, a suitable curing schedule was adopted, in the result, an ultra - high performance concrete designated rpc was successfully prepared by normal technology methods
本文基於超細粒聚密材料（ dsp ）和活性粉末混凝土（ rpc ）配製的基本原理，選用硅灰、粉煤灰、石英粉和硅酸鹽水泥，輔以高效減水劑，採用多重復合的技術路線，運用混雜鋼纖維增強理論和微集料填充密實原理，調整材料組成，優化混凝土配合比，結合適宜的養護制度，在現有技術條件下，成功制備出了rpc200材料。 -
Aggregate - to - cement ratio
砂石與水泥比例 -
The mixture designed according to low cement / aggregate ratio and fly ash / cement ratio meets the demands on strength and economy
採用低膠沙比和灰膠比組合確定混合料的配合比，既可滿足強度要求，又能達到經濟性目的。