  1. The results show that, anodic oxide films treated with atmp and dtpmp can achieve more perfect hydration resistance, especially dtpmp, which has least rising time, 7s. 4. use of dibasic ammonium phosphate and gluconic acid delta lactone to improve

    研究結果表明:相對于adp ， atmp和dtpmp明顯改善了氧化膜的耐水合特性，其中dtpmp的耐水合處理效果最好，其升壓時間為7s 。
  2. Microstructure of anodic aluminum oxide films

    鋁陽極氧化膜納米孔陣列的微細結構
  3. The important results and innovations are as follows : 1. anodic oxide films are treated with galvanization in monobasic ammonium phosphate ( adp ) solution. the effects of technologic parameters, including concen - tration and temperature of adp solution and galvanizing time on rising time of anodic oxide films are discussed

    論文的主要內容及創新性研究歸納如下: 1 .將化成箔置於磷酸二氫銨（ adp ）溶液中進行加電處理，探討了adp的溶液濃度、處理溫度和處理時間對氧化膜升壓時間的影響，並找到其最佳工藝參數。
  4. 3. diethylene triamine penta methylene phosphonic acid ( dtpmp ) is applied to hydration resistance treatment of anodic oxide films, which treating method is same as that of atmp

    3 .提出以二乙烯三胺五甲叉膦酸（ dtpmp ）為耐水合處理試劑，耐水合處理方法同atmp 。
  5. After dipped in amino trimethylene phosphonic acid ( atmp ) solution, anodic oxide films are annealed in pipe stove. the influences of concentration and temperature of atmp solution and annealing temperature on rising time, withstanding voltage and specific capacitance of anodic oxide films are studied. after hydration, anodic oxide films treated with atmp or not are analyzed by ft - ir

    2 .將化成箔在氨基三甲叉膦酸（ atmp ）溶液中浸漬，取出烘乾后再進行熱處理，研究了atmp溶液濃度、浸漬溫度和熱處理溫度對氧化膜升壓時間、比容、耐電壓的影響，找到其最佳耐水合處理工藝;採用ft - ir對水合作用后的atmp處理氧化膜和未經耐水合處理氧化膜進行了分析。
  6. The optimum concentration and temperature of dtpmp solution and optimum annealing temperature are discussed. in addition, hydration resistant effect of anodic oxide films treated with adp, atmp and dtpmp respectively is discussed through ft - ir, xps, afm and i - v characteristics testing

    探討了dtpmp溶液濃度、浸漬溫度和熱處理溫度對氧化膜升壓時間、比容、耐電壓的影響，並找到其最佳耐水合處理工藝;同時採用ft - ir 、 xps 、 afm和i - v特性測試對adp 、 atmp 、 dtpmp三種試劑對氧化膜的耐水合處理效果進行了對比研究。
  7. The results show that, the hydration resistance of anodic oxide films treated with atmp is improved greatly, the rising time decreases to 8s from 15s, which is the rising time of anodic oxide films treated with adp, and ft - ir analysis confirms that atmp treatment can inhibit oxide films from hydration effectively in boiling water

    研究發現:氧化膜經atmp處理后，其耐水合特性得到很好的提高，氧化膜的升壓時間從adp處理氧化膜的15s縮短到8s ; ft - ir分析證實atmp處理可有效阻滯氧化膜在沸水中的水合作用。
  8. How to improve hydration resistance of anodic oxide films effectively is the leading content in this paper

    本論文圍繞如何有效提高鋁電解電容器陽極用氧化膜的耐水合特性展開研究。
  9. Based on the actual state of improving hydration resistance of anodic oxide films in the world, hydration resistance and its technologies are explored and investigated. hydration resistance mechanisms and effects of technologic parameters on rising time, specific capacitance and withstanding voltage are expatiated

    根據目前國內外鋁陽極氧化膜耐水合特性改善技術的研究現狀，主要針對耐水合處理試劑及其處理工藝問題作了創新性和探索性研究，並對耐水合處理試劑的作用機理和工藝參數對氧化膜升壓時間、耐電壓及比容的影響進行了詳細研究。