cast carbide 中文意思是什麼

cast carbide 解釋
鑄態硬質合金
  • cast : vt （cast; cast）1 投，扔，擲，拋。 ★此義動詞通常用 throw cast 只用於若干特殊句子。2 丟棄，拋棄；...
  • carbide : n. 【化學】碳化物；碳化鈣；電石〈粗製CaC2〉。
  1. The particles distributed hi the matrix of grey cast iron, but some contact each other. the composite layer extend gradually into the substrate. when volume fraction of wc is 36 wt % and 27 wt %, the matrix of the composite is high chromium cast iron, consist of white carbide bars and the austenite. wc particles distributed uniformly, retaining approximately quondam granular form in the composite layer which has an evident interface area with the substrate, with good bonding strength

    對不同碳化鎢體積分數的灰鐵和低鉻鑄鐵基復合材料的微觀組織結構分析表明：碳化鎢體積分數為52時，復合層內基體為灰口鑄鐵組織，顆粒直接分佈在灰鐵基體上，部分碳化鎢顆粒有相互接觸的現象，基材與復合層之間沒有明顯的過渡；碳化鎢體積分數為36 、 27時，復合層內基體為高鉻鑄鐵，由面塊狀的奧氏體和白條狀碳化物組成，碳化鎢顆粒表面固溶於基體組織中，粒形基本保持完整，分佈均勻，與基體構成冶金結合，基材與復合層之間存在一個明顯的平緩過渡區。
  2. The strength and wear resistance of diamond drill bits for petroleum exploitation will be increased considerably when cast tungsten carbide is applied and adheres to the substrate firmly with cast tungsten carbide of 80 - 200mesh as the skelton and copper alloy as the soldering material in a process of non - pressure immersion

    石油鉆探行業用的金剛石鉆頭，用粒度為80 ? 200目的鑄造碳化鎢粉作骨架，採用無壓浸漬工藝，以銅合金作釬焊料，將鑄造碳化鎢與基體牢固結合，強度、耐磨性大大提高。
  3. The age hardening characteristic of as - cast cu20ni20mn and cu20ni35mn alloys and the interface characteristic between the alloy and cast tungsten carbide were studied, and on the basis of this study, composites of cu - ni - mn alloy reinforced with different volume fraction ( 0 - 45vol. % ) and different size ( 42 - 362 m ) of cast tungsten carbide particles were made by vacuum hot - pressing liquid sintering technology. pin on disk two body abrasion tests have been performed with different size of sic abrasive under different loads

    本文研究了鑄態cu20ni20mn和cu20ni35mn合金的時效硬化特性及其與鑄造碳化鎢的界面特性，並在此基礎上以不同尺寸（ 42 362 m ）的鑄造碳化鎢顆粒為增強體，採用真空熱壓液相燒結技術制備了不同顆粒含量（ 0 45vol . ）的鑄造碳化鎢顆粒增強cu - ni - mn合金基復合材料；以不同粒度的sic為磨料，在不同載荷條件下利用銷?盤磨損試驗機測試了復合材料的二體磨料磨損性能。
  4. Their lifetime can be prolonged if they are repaired with cast tungsten carbide powder

    採用鑄造碳化鎢修補后，可以延長使用壽命。
  5. The vc - fe surface composite shows high wear - resistance, it ' s wear - resistance is 4. 20 times as that of chilling respectively. with the content of v increasing, it ' s rigidity and wear - resistance increases continually. more vc grains gained, and well distributed, better wear - resistance the vc - fe surface composite will show. ( 7 ) surface cermet composite was formed by the means of cast - sintering technique, with the help of adding wc grains and the quantity of heat sent out from the reaction v + c vc, the carbide cermet quality percent exceeds 60 %

    在重載干滑動摩擦條件下， vc一fe表面復合材料顯示了很高的耐磨性，其相對耐磨性是可淬硬鑄鐵的4 . 2倍:隨著含v量的增加， vc一fe表面復合材料的鑄態硬度和耐磨性不斷提高， vc顆粒越多，分佈越均勻，表面復合材料的耐磨性就愈好。
  6. In order to avoid eutectic carbide, improve nodularity, increase nodule count and increase mechanical properties, three times of inoculations were adopted in the centrifugally cast nodular iron pipes production : a ) inoculation in ladle ; 2 ) pouring stream inoculation ; 3 ) in - mold inoculation

    摘要在離心鑄造球墨鑄鐵管生產中，為防止共晶滲碳體析出，改善球化，增加石墨球數，提高力學性能，採用了三次孕育： （ 1 ）包內孕育； （ 2 ）澆注時隨流孕育； （ 3 ）型內孕育。
  7. Our solid carbide tools have been widely used in aviation, space, auto, mould etc. industries, can be applied to materials of cast iron, steel, stainless steel, alloy steel, harden steel, mould steel, tool steel, bearing steel, heat - resistant alloy, titanium alloy, nickel, plastic fiber, aluminum alloy, copper

    喜威一合金刀具目前已廣泛應用於航空，航天，汽車，模具等行業，用於加工灰鑄鐵，球墨鑄鐵，碳鋼， ，軸承鋼，模具鋼，合金鋼，工具鋼，淬火鋼，調質鋼，不銹鋼，玻璃鋼，鋁合金等軟金屬，鈦合金，鎳基高溫合金。
  8. Abstract : the microstructure of as - cast high cr injection micro - alloying martensitic cast iron and the substructure of martensite in it have been observed under sem and tem. the alloying element distribution related to phase formation, as well as the various types of branch and distortion of carbide in the martensitic cast iron have been explored by using x - ray diffraction and electron probe analysis

    文摘:應用掃描電鏡和透射電鏡研究了噴射微合金化的鑄態馬氏體高鉻鑄鐵顯微組織及馬氏體的亞結構，並藉助x射線衍射與電子探針分析探討了合金元素的分佈與相形成的關系，以及碳化物的不同形式分枝與畸變。
  9. Abstract : several basic problems with the trace elements in cast irons which was studied by using thermodynamical theory was intorduced. these problems included : the solubility of trace elements in cast irons, the influences of trace elements on the crystallization temperature of molten irons, and the tendency to form carbide in molten cast irons

    文摘:介紹了運用熱力學理論研究鑄鐵中微量元素的幾個基礎問題，其中包括微量元素在鑄鐵中的溶解度、對鐵液結晶溫度的影響以及在鑄鐵溶液中形成碳化物的傾向。
  10. Cast tungsten carbide

    鑄造碳化鎢
分享友人