compatilizer 中文意思是什麼
compatilizer
解釋
相容劑-
( 2 ) when the content of organobentonite was 3wt %, the intercalation behaviors depended on the chain length of organic modifier in the bentonite and the content of compatilizer
（ 2 ）在有機膨潤土含量為3wt %時，插層的效果決定於有機改性劑烷基鏈的長度和相容劑的用量。 -
The mechanical tests result showed that when the mmt content is 2 % and the compatilizer content is 15 %, the pmc has best mechanical property. the izod impact strength is 16. 45 kj / m2 and the tensile strength is 35. 77 mpa, increasing 280 % and 4. 3 %, compared with pure pp. the pom photo indicated that the o - mmt can reduce the scale of spherical crystal of pp
以am為插層劑得到的聚丙烯蒙脫土納米復合材料中，蒙脫土保持剝離狀態，但力學性能不理想，當土含量為0 . 5時，材料的沖擊強度為9 . 58kj m ~ 2 ，拉伸強度為25 . 5mpa 。 -
The result showed that ( 1 ) organic modifier can reduce the polarity of na - bentonite, and compatilizer ( maleic anhydride grafted polyethylene ) can strengthen the polarity of polyethylene and the interface compatibility between polyethylene and bentonite. when the number of methylene groups in alkylamine was larger than 16, the intercalation nanocomposites were obtained
研究結果表明， （ 1 ）有機改性劑能夠降低鈉基膨潤土的極性，相容劑（馬來酸酐接枝聚乙烯）對增強聚乙烯的極性，增強聚乙烯和膨潤土的界面相容性有很大作用。 -
Nonpolar polypropylene has bad compatibility with mmt even after organic modification to mmt. so polypropylene ( pp ) grafting acrylic acid was produced by the suspension grafting method as compatilizer. as pp / mmt nanocomposites prepared from htab modified mmt as concerned, the interlayer spacing of mmt is 4. 61nm, 4. 2nm and 4. 09nm respectively when the mmt content is 1 %, 2 % and 3 %. so, the abtained nanocomposites has intercalated structure
當土含量為2 ，相容劑用量為15時力學性能最好，缺口沖擊強度和拉伸強度分別達到16 . 45kj m ~ 2和35 . 77mpa ，分別比純pp增加了280和4 . 3 ，蒙脫土的加入起到了增韌和增強的雙重作用。 -
( 3 ) when the content of compatilizer were 15wt % 30wt % ( to high density polyethylene ), the intercalation high density polyethylene / bentonite nanocomposites were obtained. ( 4 ) the intercalation nanocomposites were obtained after bentonite compounded with low density polyethylene and liner low density polyethylene respectively
（ 3 ）當相容劑含量為15wt % 30wt % （對于高密度聚乙烯） ，能夠得到插層型高密度聚乙烯/膨潤土納米復合材料。 （ 4 ）低密度聚乙烯和線型低密度聚乙烯與膨潤土復合后也能夠分別獲得插層型納米復合材料。