  1. Abstract : based on the analysis of the main failures discovered in pavement on steel deck plate and the demanding service condition of the pavement on steel deck, high - temperature rutting test, low - temperature bending test and controlled stress flexural fatigue test are used to study the performance of asphalt mixtures modified by epoxy resin including high - temperature stability, low - temperature cracking - resistance, and fatigue cracking - resistance, which are served to evaluate the modification effect of epoxy resin of different contents. with the addition of epoxy resin, all the three performances are improved greatly. however, when the amount of epoxy resin added is over a certain value, the modification effect will be stable with no extra benefit detected. finally, in terms of the properties of the three respects, 20 ?, 30 ?, 30 ? are given separately as the proposal adding contents

    文摘:在分析鋼橋面鋪裝層主要病害和特殊工作環境的前提下，分別採用高溫車轍試驗、低溫小梁彎曲試驗和控制應力小梁彎拉疲勞試驗，研究了不同環氧樹脂摻量下的環氧樹脂改性瀝青混合料的高溫穩定性、低溫抗裂性和抗疲勞性能.試驗結果表明:環氧樹脂對這3個方面都有很大的改進效果，但改性效果和樹脂的添加量並不是一個無限遞增的關系，當添加量超過一定數值以後，改性的效果將趨于平穩.最後就高溫、低溫、疲勞3個方面分別提出環氧樹脂添加量為20 ? ， 30 ? ， 30 ?的建議值
  2. Based on the analysis of the main failures discovered in pavement on steel deck plate and the demanding service condition of the pavement on steel deck, high - temperature rutting test, low - temperature bending test and controlled stress flexural fatigue test are used to study the performance of asphalt mixtures modified by epoxy resin including high - temperature stability, low - temperature cracking - resistance, and fatigue cracking - resistance, which are served to evaluate the modification effect of epoxy resin of different contents. with the addition of epoxy resin, all the three performances are improved greatly. however, when the amount of epoxy resin added is over a certain value, the modification effect will be stable with no extra benefit detected. finally, in terms of the properties of the three respects, 20 ?, 30 ?, 30 ? are given separately as the proposal adding contents

    在分析鋼橋面鋪裝層主要病害和特殊工作環境的前提下，分別採用高溫車轍試驗、低溫小梁彎曲試驗和控制應力小梁彎拉疲勞試驗，研究了不同環氧樹脂摻量下的環氧樹脂改性瀝青混合料的高溫穩定性、低溫抗裂性和抗疲勞性能.試驗結果表明:環氧樹脂對這3個方面都有很大的改進效果，但改性效果和樹脂的添加量並不是一個無限遞增的關系，當添加量超過一定數值以後，改性的效果將趨于平穩.最後就高溫、低溫、疲勞3個方面分別提出環氧樹脂添加量為20 ? ， 30 ? ， 30 ?的建議值
  3. Effect of fly ash on the cracking resistance of concrete

    混凝土抗裂的粉煤灰效應
  4. Standard test method for outdoor evaluation of tire sidewall component cracking resistance

    輪胎側壁組件抗斷裂性能的室外評定標準試驗方法
  5. Standard test method for determining stress - corrosion cracking resistance of heat - treatable aluminum alloy products using breaking load method

    用破壞載荷法測定可熱處理鋁合金製品的抗應力腐蝕開裂特性的標準試驗方法
  6. Furthermore, the fatigue parameters of polyester fiber rein - forced asphalt concrete are decreased, which imply that the fatigue cracking resistance of asphalt concrete is improved

    同時，聚酯纖維瀝青混凝土的損耗模量降低，其抵抗疲勞開裂的能力增強。
  7. Standard practice for evaluating stress - corrosion - cracking resistance of metals and alloys in a boiling magnesium chloride solution

    評定在沸騰的氯化鎂溶液中金屬及其合金的抗應力腐蝕斷裂
  8. Standard practice for evaluating stress - corrosion cracking resistance of low copper 7xxx series al - zn - mg - cu alloys in boiling 6 % sodium chloride solution

    在6 %沸騰的氯化鈉溶液中進行鋁鋅鎂低銅合金的應力腐蝕斷裂試驗的標準實施規程
  9. The experimental result indicate that the working characters of the test floor slab is typically two - way obviously, the floor slab that is reinforced two - way by setting transverse steels through the rectangular cores in the ribs of the precast slabs, has excellent bulking property, high bearing capacity, cracking resistance and so on

    試驗研究表明，試驗樓蓋在加載過程中呈現了明顯的雙向受力特徵; pk預應力疊合樓蓋通過在預制構件板肋預留長方形孔穿置橫向鋼筋實現雙向配筋具有良好的整體性能，還具備承載力高和抗裂性能良好等特點。
  10. Experimental investigation on sulfide stress corrosion cracking of 16mn hydrogen induced cracking resistance steel

    鋼硫化物應力腐蝕開裂實驗研究
  11. Some conclusions are drawn : the compressive strength and flexural strength of cubic specimens of steel fibre reinforced concrete increase with the dosage of steel fibre ; without change of dosage of steel fibre, the elastic modulus of steel fibre reinforced concrete increases with the concrete age ; steel fibre reinforced concrete is of obvious function in cracking resistance, but there is no obvious function in avoidance of cracking ; for both common concrete and steel fibre reinforced concrete, the variation of the internal temperature is different from that of the external temperature before the initial set of concrete, and the internal strain of both two kinds of concrete is great, and, in general, the variation of strain of common concrete is much greater than that of the steel fibre reinforced concrete ; after the initial set of concrete, the variation of the internal temperature of both two kinds of concrete is similar to that of the external temperature, and the variation of the internal strain is relatively small

    結果表明：鋼纖維混凝土立方體的杭壓強度、抗彎強度隨著鋼纖維摻量的增加而增大；在鋼纖維摻量不變的情況下，鋼纖維混凝土的抗壓彈性模量會隨著齡期的增加而提高；鋼纖維對混凝土的阻裂作用很明顯，而對混凝土起裂的限製作用不明顯；在混凝土初凝之前，無論是普通混凝土還是鋼纖維混凝土，內部溫度的變化規律與外界溫度的變化規律不同，並且此階段混凝土內部應變的變幅很大，普通混凝土應變的變幅要比鋼纖維混凝土應變的變幅大得多；在混凝土初凝之後，無論是普通混凝土還是鋼纖維混凝土，內部溫度的變化規律與外界溫度的變化規律相同，並且此階段混凝土內部應變的變幅很小。
  12. Good toughness and thermal cracking resistance. used in the stands of prefinish rolling. suitable for hot rolling thread steel

    具有優良的韌性和抗熱烈紋能力，適用於預精軋機架和熱軋螺紋鋼
  13. Abstract : in this paper, the road performence of cao and fly - ash stabilizing aggregate is discussed, in terms of strength, strength at low temperature, postponing shaping time, and cracking resistance

    文摘:通過大量試驗，分析研究了生石灰-粉煤灰碎石的路用性能，從強度、低溫強度、悶料時間、抗裂性能等方面對生石灰-粉煤灰碎石的路用性能進行了分析研究
  14. Research on cracking resistance performance of super vertical - distance pumped steel fiber concrete

    超高程泵送鋼纖維混凝土的抗裂性能
  15. The development of mortar shrinkage and cracking level is attributed to cracking total weigh w. the experiment results showed that above - mentioned test method can evaluate effectively the cracking status of mortar, the cracking resistance of polymer modified mortar is better than traditional mortar

    採用環形約束裝置測定砂漿的開裂情況，並應用開裂總權值w表徵砂漿收縮開裂程度發展情況，研究結果表明:該方法可有效評價聚合物改性砂漿與普通砂漿的開裂情況，聚合物改性砂漿的抗裂性要明顯優于普通砂漿。
  16. Standard test method for cracking resistance of leather

    皮革耐裂性的標準試驗方法
  17. It can be used to improve the concrete cracking resistance and seepage resistance

    具有改善混凝土抗裂能力、抗沖擊抗磨耗能力等作用。
  18. Influence of ageing on fracture toughness and stress corrosion cracking resistance of b95 forging

    鍛件斷裂韌性和抗應力腐蝕性能的影響
  19. The experiment test results of mechanical properties and durability of hprrc show : no matter at early age or later age, the ration of flexural strength to the cubic compression strength of hprrc is higher than ordinary concrete, and the brittleness of hprrc is reduced ; the bond performance of new - old concrete interface and chloride permeability are good ; its resistance to freeze and thaw, permeability are all excellent ; its volume stability is improved, and its cracking resistance is good

    配製出和易性優良（坍落度30mm ） 12 48h能滿足開放交通的hprrc 。 5 、 hprrc力學性能、耐久性能試驗結果表明：無論早期還是後期，其折壓比均比普通砼的有所提高，脆性有所降低；新老砼粘結性能優良；並具有優異的抗凍性、抗滲性、耐磨性，抗氯離子滲透能力強；體積穩定性大為提高，抗裂性好。
  20. The material also is recommended for contour extrusion and for blow molding of toys, gaskets and other parts requiring permanent flexibility, stress cracking resistance and low temperature toughness

    這種材料也被推薦用於製造玩具，墊圈和其他要求有長期的彈性，抗應力裂紋和低溫韌性的輪廓擠出成型和吹塑成型中。