Results show that self - crosslinkable latex at room temperature with high elasticity can be prepared when amount of butyl acrylate is 60 %, and amount of methyl methacrylate is 40 %, and mass ratio of nonionic emulsifier to anionic emulsifer is 3 : 1, and amount of initiator is 0. 6 %, and amount of self - crosslinkable monomer and protective colloid is 2 % and 0. 4 % respectively
研究結果表明：當丙烯酸丁酯的質量為60 % ，甲基丙烯酸甲酯的質量為40 % ，非離子乳化劑和陰離子乳化劑的質量配比為3 : 1 ，引發劑的質量為0 . 6 % ，自交聯單體的質量為2 % ，保護膠體的質量為0 . 4 %時，可以制備出高彈性自交聯乳液。 -
Influences of content of soft monomer and hard monomer, emulsifiers, initiators, self - crosslinkable monomer and protective colloid on the properties of emulsion are studied
研究軟硬單體含量、乳化劑、引發劑、自交聯單體、保護膠體等對聚合物乳液性能的影響。 -
Self - crosslinkable latex at room temperature with high elasticity is prepared when n - hydroxymethyl acrylamide is used as self - crosslinkable monomer, and poly solidum maleate is applied as protective colloid, and pre - emulsified and semi - continuous seeded emulsion polymerization is adopted
採用n -羥甲基丙烯酯胺為自交聯單體，聚馬來酸鈉為保護膠體，採用預乳化半連續種子乳液聚合工藝，制備出高彈性室溫自交聯乳液。