electrochromic 中文意思是什麼

electrochromic 解釋
電致彩色發光
  1. Under the applied voltage of 2v, the duration of colored process and bleaching process of the semisolid - state smart window was 2s and 1. 5s respectively, which denoted rapid response velocities. researches on the glass / ito / wo3 / linbo3 / niox / au all solid - state smart window were referred to the effect of each film ' s thickness on the device ' s electrochromic properties. through the test of the visible light transmittance of the colored state and bleaching state of the device, it proved good electrochromic capabilities with the dynamic optical density changed between 0. 2 - 0. 5

    並在此基礎上繼續研究了glass ito wo _ 3 linbo _ 3 nio _ x au結構的全固態智能窗器件模型，對于各薄膜層厚度對于器件電致變色性能的影響做了初步的研究，測試了器件可見光范圍內的著色褪色透射光譜，光密度變化量在0 . 2 0 . 5范圍內，表明器件具有良好的電致變色性能。
  2. Standard test method for measuring the uniformity of an absorptive electrochromic coating on a glazing surface

    拋光表面上吸收性電致變色塗層均勻性測量的標準試驗方法
  3. The intercalation of peo leads to the structural rearrangement, resulting in the improvement of the li + ions content in the films. moreover, the intercalation of peo enhances the electrochromic efficiency, resulting in the improvement of electrochromic behavior of the films

    同時普遍提高了復合薄膜在近紫外和近紅外區域的吸收率，增強了薄膜在近紫外區的陰極電致色，提高了薄膜的電致變色效率，改善了薄膜的電致變色性能。
  4. The stretching vibration of v = o shifts to lower wavenumbers, which is contributed to the oet v : = o bonding interaction. the intercalation of peo effectively shields the electrostatic interaction between li + ions and v2o5 layers, resulting in the improvement of the cycling reversibility and stability of li + ions insertion / extraction in the interlayer of v2o5 xerogel and the improvement of electrochromic behavior of the films

    通過電學、電化學和光學性能測試結果表明: peo的嵌入，有效屏蔽了vzos層對li十離子的靜電作用及peo與li十離子之間產生的絡合作用，大大提高了li +離子在氧化物層間的嵌入容量、嵌入/脫出可逆性和穩定性，有效提高了薄膜的電致變色性能尤其是在近紫外區的陰極電致變色性能。
  5. Four kinds of optical limiter had been researched including suspending inorganic particles, semiconductor / electrochromic polymer multiplayer device, porphyran

    研究發現，卟啉類反飽和吸收材料有很好的光限幅作用。
  6. The crystal grain boundary of v2o5 films was melted and disappeared as increasing the deposition temperature, and the crystalline v2o5 films can be obtained by deposition at > 300. these films showed excellent cathode and anodic electrochromic performance at different wavelength region

    而襯底溫度升高促進薄膜晶體顆粒長大、熔結，晶粒邊界消失，在較高襯底溫度（ 300 400 ） ，得到連續的結晶性能良好的v _ 2o _ 5薄膜。
  7. To find the parameters of preparation and annealing process associated with the best electrochromic properties of these films, following researches and experiments were carried out : to compare the visible light transmittance of the colored state with bleaching state of the electrochromic films which were annealed at different temperatures and for different duration, to count the dynamic optical density change, and to test the i - v relations of these films " electrochromic cycles and their colored / bleaching response time

    對經過不同熱處理溫度和不同熱處理持續時間得到的薄膜樣品的著色褪色可見光范圍內透射光譜的比較，計算薄膜動態光密度變化量的大小，測試薄膜著色褪色循環伏-安關系以及薄膜著色褪色響應時間的快慢，尋求到薄膜呈現最佳電致變色性能時所對應的制備參數與熱處理參數。
  8. Electrochromic display ecd

    電鉻顯示器
  9. Standard test methods for assessing the durability of absorptive electrochromic coatings on sealed insulating glass units

    密封隔熱玻璃元件上吸收的電鍍鉻塗層穩定性評價的標準試驗方法
  10. Electrochromic properties of doped tungsten oxide thin films

    摻雜氧化鎢薄膜的電致變色特性
  11. Tungsten oxide and nickel oxide films were prepared by electron beam evaporation method, and the effect of annealing techniques of the electrochromic properties of these films was discussed

    本論文利用電子束蒸發方法制備氧化鎢、氧化鎳薄膜的基礎上，研究了熱處理工藝對于薄膜電致變色性能的影響。
  12. A new method of mix - oxide doped electrochromics is described in this paper. the electrochromic layer and the ionized conductance layer are doped with oxide and metal respectively, which highly improve the characters of response and chromic transitivity of the electrochromic apparatus. finally, the experimental results are presented

    本文論述採用混合氧化物摻雜的新方法，對電致變色層和離子導電層分別摻入氧化物和金屬，使電致變色器件響應速度、增大著色透過率變化等方面的特性得到很大改善.最後給出實驗結果
  13. 194 f - standard test method for assessing the current - voltage cycling stability at 90c of absorptive electrochromic coatings on sealed insulating glass units

    密封絕緣玻璃裝置有吸收力的電致變色覆層在90
  14. Standard test method for assessing the current - voltage cycling stability at room temperature of absorptive electrochromic coatings on sealed insulating glass units

    密封絕緣玻璃裝置有吸收力的電致變色覆層在室溫下的電流-電壓循環穩定性評估的標準試驗方法
  15. But if we want to make this product in practice, the all - solid state electrochromic device must be making

    但是要將電致變色材料向實用化推廣，必須制備出全固態電致變色器件。
  16. Inorganic - organic nanometer hybrid materials summarize the characteristics of inorganic material, organic material and nanomaterial, so they have new applications in many fields such as electronics, chemistry, catalyst, mechnics, biochemistry, etc. molybdenum trioxide which has good light sensitivity is widely used in preparing the photochromic and electrochromic materials

    無機?有機納米雜化材料綜合了無機、有機和納米材料的優良特性，廣泛應用於電子、化學、催化、生物、機械等領域。三氧化鉬因具有優良的光學特性而被廣泛地用來研究制備光致、電致變色材料。
  17. Electrochromic properties of electron beam evaporated tungsten oxide and nickel oxide films

    氧化鎳薄膜的電致變色性能
  18. At present, the investigation about this aspect is concentrate on the pure inorganic cathodal electrochromic materials like wo3 and organic electrochromic materials like prussian blue and polyaniline. but for the doped electrochromic materials, the research is very lack

    關于這方面的研究卻主要集中在以wo _ 3為代表的一元無機陰極電致變色材料和普魯士蘭、聚苯胺為代表的有機電致變色材料上，對多元的電致變色材料的研究較少。
  19. Electrochromic properties of wox - ti films

    薄膜的電致變色性能
  20. Influence of oxygen content and titanium doping on electrochromic properties of wo3 films

    3電致變色性能的影響