film grain size 中文意思是什麼
film grain size
解釋
膠片顆粒大小-
The desensitized explosive petn film was prepared by physical vapour deposition ( pvd ) technology, and sem was used to analyze the microstructure and grain size of petn film
摘要採用物理氣相沉積（ pvd ）技術研製了鈍化太安炸藥薄膜，對薄膜的微觀結構和顆粒粒度進行了分析，對顆粒粒度與薄膜爆轟波穩定傳播臨界尺寸的關系進行了探索。 -
The zn / o ratio, c - axis orented and stress were improved by annealing, and also redusing the defect of zno flim, increasing the size of grain. but too high annealing temperature was adverse to recrystallization of zno thin film
退火能改善zno薄膜的鋅氧比、 c軸的擇優取向和應力狀態，減少薄膜中的缺陷，使晶粒長大，但是過高的退火溫度不利於zno薄膜的重結晶，使zno薄膜的質量變差。 -
The results are as follows : ( 1 ) bst thin film prepared by pulsed laser deposition is well crystallized. the average grain size is 100nm and the surface roughness is about 10nm. when the electric field intensity is 3v /, the tunability of the thin film is about 30 % and the loss tangent is about 20 % under room temperature
研究結果如下： （ 1 ）採用脈沖激光沉積法制備的bst薄膜結晶良好，晶粒尺寸在100左右；表面粗糙度約為10 ；室溫下，當直流電場為3v /時介電系數變化率約為30 % ，介質損耗約為20 % 。 -
Thin films with thickness of 0. 31m and 0. 36m respectively on si substrate, have been successfully prepared by a sol - gel spin coating method. cubic nanocrystals can be obtained at relatively low sintering temperature with an average grain size of about 47 nm and 51 nm respectively. the aluminia - doped scsz thins film are the same dense as the scsz thin films. however, there are a small amount of pinholes found in the microstructure of the titania - doped scsz films
0 . 70固體電解質納米晶薄膜。燒結實驗結果表明，兩種薄膜均在650以上開始晶化，溫度越高，晶化越完全，在800可完全晶化所得納米晶顆粒呈純的螢石結構立方相鋁和鈦摻雜的納米晶顆粒的平均大小分別為47和51nm 。 -
The patient is in or two side breast can feel size to differ, soft hard the bump with differ, not quite clear dividing line, the surface has little grain it seems that, do not have adhesion with film of the skin, muscle, press with finger after pressing, feel aching namely
病人在一例或兩側乳房可摸到大小不等、軟硬不一、界限不太清楚的腫塊，表面似乎有小顆粒，與皮膚、筋膜無粘連，用手指按壓后即感到疼痛。
分享友人