In this paper a lot of experimental data about a - al2o3 crystal with adulterant and zno crystal were acquired by studying the effects of the hydrothermal condition on the synthesized crystal. this paper also will provide guidance for hydrothermal industrialization and researching hydrothermal kinetic process
本文通過研究合成條件對合成晶體的影響，獲得了大量的有關合成摻雜- al _ 2o _ 3和zno晶體的實驗數據。論文的完成將對進一步完成生產性工藝和探索水熱合成反應動力學過程有重要的指導意義。 -
In this paper, oxid crystals were synthesized by the hydrothermal method, and the effects of the hydrothermal condition on shape and quality of crystal were studied by changing experimental temperature and mineralizer. on the base of these works the blue sapphire dopped with fe, ti and sapphire dopped with ti were synthesized. meantime, the effects of ti, fe - dopped on sapphire and what lead to the blue of sapphire were studied
本文採用水熱法合成了- al _ 2o _ 3和zno晶體，通過改變溫度和礦化劑條件研究了水熱條件下溫度和礦化劑對- al _ 2o _ 3和zno晶體合成的影響；在此基礎上通過摻雜致色元素，合成了藍色藍寶石、鈦藍寶石，並研究了fe 、 ti等致色離子對藍寶石晶體界面形態和質量的影響，分析了藍寶石的致色原因。 -
An isotropic viscoelastic model coupled with hydrothermal effects
含濕熱效應的各向同性耦合粘彈模型 -
3. pani nanofibrils were synthesized for the first time by using chemical oxidative polymerization under hydrothermal conditions. the effects of concentration of aniline, doped acid and the reaction time on the morphology of pani were researched
3 .在水熱條件下通過化學直接氧化的方法得到聚苯胺納米纖維，討論了苯胺的濃度，摻雜酸和濃度以及水熱時間對聚苯胺納米纖維生成的影響。 -
The effects of reactive conditions on the products were discussed and the proper conditions are determined. we primarily synthesize a series of ba1 - xsrxti1 - ysnyo3 solid solutions nanopowder by low - temperature / low - pressure hydrothermal method under the condition of 150, 0. 5mpa
採用低溫一低壓水熱合成法，在150 ， o . smpa以下合成了一系列bal一xsrxtil一ysnyo3固溶體納米粉末，由於摻雜離子均勻進入母體晶格以及材料的結晶更完整，使得介電性能明顯改善，不僅t 。 -
In order to meet the requirement of nano - hexaferrites, hydrothermal method and sol - gel self - propagating high - temperature synthesis method were applied. by studying the effects of different precursors, ph value, temperature and time, the optimum conditions were determined, the structure of crystals was studied by x - diffract aat the same time the morphologic and the diameter of crystals were studied by tem
使用x一射線衍射鑒別晶體結構，通過透射電子顯微鏡觀察粒子的形貌與大小， x一射線衍射鑒別晶體是鋇鐵氧體，透射電子顯微鏡觀察粒子的形態與大小， ，發現粒子分散性較好，結晶性良好，形貌為六角型，通過統計計算粒子粒徑，粒子大小處于納米級，平均粒徑為70nm 。