The diffusion welding behavior of single - crystalline cu to single - crystalline - aio with a nb film interlayer and the joint microstructure properties were studied by tem, sem / eds analyses and four - point bend testing. the nb film interlayer deposited by electron beam evaporation on the ceramic side prior to diffusion welding was found to be olycrytalline and fiber - textured after diffusion bonding, with the close - packed plane ( 110 ) being parallel to the ( 0001 ) basal plane of - aio
擴散連接技術是一門邊緣科學，涉及材料、擴散、相變、界面反應、接頭應力應變等各種行為，工藝參數多，雖然已經進行了大量的試驗研究，但卻對各種材料的連接機理尚未有明確的認識，為此人們試圖藉助于計算技術，對接頭行為進行數值模擬，以便找到共同規律，對擴散連接過程及質量進行預測與實時控制。 -
Copper has been deposited on surface of the al mmcs as interlayer by magnetron sputtering, tlp bonding of al mmcs with these interlays, the joints shear strength of tlp bonding using deposited film was as much as the joint shear strength of tlp bonding using cu foil. removing the oxidation on the surface before deposition, copper was coated by magnetron sputtering as tlp bonding interlayer
待連接表面通過磁控濺射法沉積銅膜作為中間層進行瞬間液相連接，得到的接頭強度與銅箔中間層進行瞬間液相連接得到的接頭強度相當，而使用磁控濺射法去除待連接表面氧化膜后沉積銅膜作為中間層進行瞬間液相連接的接頭強度提高7 . 6左右。 -
It requires compatible part and support materials, subject to the constraints of the deposition and removal processes. the constraints on part and sacrificial support materials were identified and a compatible material combination was developed : unsaturated polyester and wax. some other investigation is conduct, such as the effect of additive on the cure of polyester, the effect of the filling on strength and shrinkage. the part strength is determined both by the bulk material properties of the part materials and by their interlayer bonding
從分析材料的選擇機制出發，本文經過大量的實驗分析，選擇了一組較好的材料組合：不飽和聚酯樹脂與蠟的組合，通過實驗分析了引發劑、促進劑對其固化過程的影響以及填料對其強度和收縮率的影響，通過測試，分析了材料的粘接強度，為工藝實現提供重要依據。 -
The stretching vibration of v = o shifts to lower wavenumbers, which is contributed to the oet v : = o bonding interaction. the intercalation of peo effectively shields the electrostatic interaction between li + ions and v2o5 layers, resulting in the improvement of the cycling reversibility and stability of li + ions insertion / extraction in the interlayer of v2o5 xerogel and the improvement of electrochromic behavior of the films
通過電學、電化學和光學性能測試結果表明: peo的嵌入，有效屏蔽了vzos層對li十離子的靜電作用及peo與li十離子之間產生的絡合作用，大大提高了li +離子在氧化物層間的嵌入容量、嵌入/脫出可逆性和穩定性，有效提高了薄膜的電致變色性能尤其是在近紫外區的陰極電致變色性能。 -
Effect of bonding state between titanium interlayer and cemented carbide substrate on the adhesion of cvd diamond film
鈦過渡層與硬質合金基體表面結合狀況對金剛石薄膜附著力的影響 -
Montmorillonite ( mmt ) clay is an important class of lamellar inorganic compounds, contains negatively charged layered silicates, which are bonded with metal cations such as na + or ca2 + by ionic bonding. whose interlayer spacing can be modified by cation exchange. when the mmt is exchanged with cations, its inner layer spacing becomes large enough to be penetrated by a monomer
蒙脫土（ montmorillonite ， mmt ）是一種天然礦物，具有層狀結構，層間靠吸附陽離子如na ~ + 、 ca ~ （ 2 + ） 、 mg ~ （ 2 + ）等來維持電荷平衡，這些離子可與其它陽離子進行交換，使有機單體分子進入層間，聚合后即可形成有機無機納米復合材料。