  1. In this thesis, through the technique ' s of compressing molding, the processing parameter and the mixture ratio of magnetic powder on magnetic properties of four kinds of binary composite bonded magnets ( ndfeb alnico ferrite smco ) were studied. the experiment results were analyzed by the method of polynomial fit. the following major achievements were attained

    本文採用模壓成型工藝對常見的四大永磁材料? ?釹鐵硼、鋁鎳鈷、鐵氧體、釤鈷進行了兩兩復合粘結，研究了工藝參數及磁粉配比對磁性能和溫度系數的影響，並通過計算機軟體進行擬合分析，得到了如下主要結果。
  2. The influnence of coupling agent, binders, curing process, formation process and the size of ndfeb powder on ndfeb bonded magnet has been systematically studied by a lot of experiments. the bonded magnet from rapid quenched ndfeb has been produced, and the influence of the technique factors such as coupling agent, coupling process, powder particle size, binder, solidification process, formation process on its properties has been analysised by means of sem, dgn - 3 magnetic properties analysis, compressive strength measurement, etc

    本文通過大量的試驗，對各向同性ndfeb粘結磁體用偶聯劑、粘結劑、固化劑，以及固化工藝、成型工藝及其粒度對磁體性能的影響進行了多方面詳細的研究。在不同工藝條件下制備粘結磁體的基礎上，利用磁性能測試儀、力學性能測試設備和掃描電子顯微鏡等測試分析手段，研究了粘結方法制備ndfeb磁性材料的制備工藝，探討了偶聯劑、磁粉粒度、粘結劑、固化劑、固化工藝和模壓工藝等對ndfeb磁體磁性能及力學性能的影響。
  3. However, the green compact ' s density has little effect on the highest sintering temperature and time. after optimizing the technological technique, the parameters on microwave magnetic sintering of ndfeb magnets were chosen : the powder with average particle size of 3 m was isostatically pressed at 2000kg / cm2, and the shape of the green compact is 18 6mm

    進行工藝優化后，我們所選用的微波燒結參數為：微波功率2kw ，粉體的平均粒徑3 m ，壓型壓力2t cm ~ 2 ，初坯為18 6mm的圓柱體，燒結最高溫度約為900 ，燒結的時間70s左右。