Base on discuss, choosing mongolian scotch pine and manchurian ash as experiment species, using three kinds of wood fire - retardant treatment methods which included soaking at some pressure, pressurized soaking under ultrasonic wave and the pressurized soaking under ultrasonic wave after treated by microwave, the result is that ultrasonic wave may apply in wood fire - retardant treatment production
在討論的基礎上，以樟子松和水曲柳為木材試樣，選擇壓力浸漬、超聲波加壓浸漬和微波處理后超聲波加壓浸漬3種木材阻燃處理方法，經過試驗，說明在生產阻燃木材的浸漬方法中引入超聲波技術是可行的。 -
The approaches of enhancing the mechanical properties of ramie and flax composites were studied in this paper. the effects of surface pretreatment, fiber content, molding temperature and pressure as well as the effect of electron beam, microwave and ultrasonic wave on the mechanical properties of the composites were explored. the experimental results show that : 1
本文以苎麻、亞麻纖維為增強材料，線性低密度聚乙烯（ lldpe ）為基體，研製了兩種麻纖維層壓復合材料，研究了麻織物表面處理、纖維含量、成型溫度、成型壓力等對該復合材料力學性能的影響，得到了性能較為優異的麻纖維復合材料，探討了復合材料的增強機理。 -
The presence of microwave or ultrasonic wave, the inter - and intra - molecular complexation of cellulose molecules through hydrogen bonding is weakened, and the complexed polymer of cellulose and nylon formed in situ. the yield strength and young ' s modulus of the ramie / nylon / lldpe composites are increased from 9. 68 mpa, 260 mpa to 15. 7 mpa and 722 mpa respectively
經微波輻照或超聲波處理后，苎麻纖維素氫鍵被削弱，與尼龍形成氫鍵復合物，增強了苎麻尼龍電子束輻照lldpe復合材料體系的相容性，屈服強度、楊氏模量從9 . 68mpa 、 260mpa提高到15 . 7mpa 、 722mpa 。