mortar admixture 中文意思是什麼
mortar admixture
解釋
灰漿附加劑-
The results indicate that the strength of mortar with early - strength admixture and uea expansion admixture will improve largely
結果表明，摻有早強型減水劑和uea膨脹劑的砂漿的強度有了較大程度的提高。 -
This kind of adglutinate mixed with u expansion admixture can grip anchor bolts tightly even underwater, as can be seen from the pull - out type tests for anchor bolts when the mortar age is over 10 days. ( 2 ) the author lays the supporting piles as a arched shape
將摻加了u型微膨脹劑的砂將作為錨桿水下膠結物，由錨桿齡期10天的抗拔試驗結果可以看出，這種膠結物的握裹效果很好。 -
The research result indicated that on the condition of the same mortar fluidity, the preventing effects of mineral and superplasticizer compounded on aar are better than that of mineral used singly, the preventing effects of mineral admixture and entraining agent compounded are better than that of mineral admixtures used singly, the preventing effects of mineral and superplasticizer and entraining agent compounded are lower than that of mineral admixture and entraining agent compounded. the research achievement has some guiding sense on the recognition of aar prevention in pumping hpc and the researches of test methods for determining the alkali reactivity of aggregate used in hpc
研究結果表明：在相同砂漿流動度條件下，減水劑與礦物摻合料復合使用對堿?骨料反應的抑制作用大於礦物摻合料單獨使用的抑制作用；引氣劑與礦物摻合料復合使用對堿?骨料反應的抑制作用優于礦物摻合料單獨使用的抑制作用；減水劑、引氣劑與礦物摻合料三元復合使用對堿?骨料反應的抑制作用小於引氣劑與礦物摻合料二元復合使用的抑制作用。 -
On the other hand, through inhibted performances of concrete and mortar, the permeability refutations with different w / c, ages, admixture, and physics chemistry absorb regulation of different viscosity permeable liquid, the liquid - gas method is proved science and accuracy. because adopting with liquid - gas method it case clearer concrete permeability regulation. different concretes relativity is more exact and more efficiency and fixed quantity
另一方面，我們利用混凝土所固有的性質：不同水灰比混凝土、砂漿、抗滲性能規律；不同齡期混凝土的抗滲規律；不同外加劑、摻合料抗滲性能之間相互對比規律；不同黏度滲透液物理化學吸附對測試結果影響的規律；用規律來映證溶液氣壓法的科學性，準確性。 -
According to each ingredients ( water retaining admixture, polymer, inorganic mineral ) " effect to mortar ' s behaviors ( water relentivity, strength, contractility ) in exclusive mortar " s composite addition, the text defines each ingredient ' s quantity scope, then define the mix through cross experiment. we compared the aac exclusive mortar ' s behaviors such as water relentivity, compressive strength, binding strength, shrinkage, flexural strength and others to ordinary mortar ' s ones, it turn out to be that there is much improve in former ' s behaviors such as water relentivity, compressive strength, binding strength, shrinkage, flexural strength etc, it also shows that the aac exclusive mortar can improve the crack in aac brick walling to a certain degree
並根據專用砂漿中復合外加劑的各個組分（保水劑、聚合物、無機礦物等）對砂漿主要性能（保水性、強度、收縮性、抗彎性等）的影響來確定每個組分的摻量范圍，再通過正交實驗確定最佳配合比，然後就普通砂漿與專用砂漿的保水性、抗壓強度和粘結強度、收縮值、抗彎曲性能以及其它性能進行了對比，對比結果表明專用砂漿的保水性、抗壓強度和粘結強度、收縮值、抗彎曲性能以及其它性能較普通砂漿都有了很大的提高，說明加氣混凝土砌塊專用砂漿在一定程度上可以改善加氣混凝土砌塊墻體的開裂情況。 -
Abstract : based on composite testing of naphthalene superplasticizer and different retarders as well as retarding water reducer, in which the overall amount of admixture is certain, this paper analyzes the influence of these multicomponent admixtures on flowability of neat cement 、 retarding action and development of strength of colloidal mortar. the result shows that compatibilities of different components are different, and composition effects are also different
文摘:在總摻量一定的情況下，就萘磺酸鹽高效減水劑與不同緩凝組分、緩凝型減水劑等復合后對水泥凈漿流動度、緩凝作用、膠砂強度發展等性能的影響作用進行了試驗分析，結果表明各不同組份復合的相容性不同，復合效應也存在差別。 -
The homogeneous characteristics of polycarboxylic acid type waterproofing agent are measured according to gb / t 8077 ? 2000 concrete admixture homogeneous experimental method, the technical characteristics of polycarboxylic acid type waterproofing agent are checked depending on jc474 ? 1999 mortar and concrete waterproofing agent. the result shows that polycarboxylic acid type waterproofing agent is provided with good anti - permeability
對試制樣品按gb / t8077 ? 2000 《混凝土外加劑勻質性試驗方法》標準檢測多元羧酸系防水劑的勻質性，按jc474 ? 1999 《砂漿、混凝土防水劑》標準檢測多元羧酸系防水劑的技術性能。 -
By research these, wocan know : 1 ) in different fineness cement, the dosage of mineral admixture improve the fluidity of cement mortar. when the dosage reach 50 %, the effect of mineral on fluidity can be better than the changing fineness of cement. 2 ) to different fineness and dosage mineral, the improve of mineral can improve the compatibility
通過研究結果發現： 1 ）對于不同細度的水泥，當礦物的摻量達到50以後，礦物摻合料對水泥膠砂流動度的影響顯著，而水泥細度的變化對相容性的影響較小。 -
Their effects on the chemical shrinkage, self - shrinkage, hole structure of cement stone and on the shrinkage of mortar and concrete were also studied thoroughly, and a concrete admixture with high performance of crack - resistant and water - repellent was prepared
通過它們對水泥石的化學收縮和自收縮、孔結構以及對砂漿及混凝土的收縮性能的深入研究配製出了一種性能優良的混凝土抗裂防水外加劑。 -
Water - repellent admixture for mortar and concrete
砂漿混凝土防水劑 -
According to standard jc474 - 1999 " water - repellent admixture for mortar and concrete ", properties of the admixture were measured and they all satisfied with the specified standard of first quality product
依據jc474一1999 《砂漿、混凝土防水劑規定方法》 ，對所配製的外加劑測定，其各項性能符合該標準中規定的一等品的要求。 -
To significantly improve both strength and durability of repair interfacial layer between old and new concrete, two attempts were firstly put forward in this thesis : ( 1 ) a kind of new modified primer would be produced by introducing shrinkage reducing admixture into cement mortar, which may both reduce the shrinkage of the interfacial layer, and lessen the content of large crystal in the repaired interface layer, accordingly, remarkably increase the van der waals force of interfacial layer
為大幅度提高新老混凝土修補界面層的強度和耐久性，本文首次提出並實現兩個設想： （ 1 ）以國產減縮劑為外加劑，配製新型改性水泥砂漿界面劑。該界面劑既能減少界面層宏觀干縮裂縫，又不增加大晶體，使界面層形成密實的微細觀結構，顯著提高粘結界面層內晶體間的范德華力。