optical bleaching 中文意思是什麼
optical bleaching
解釋
光學增白-
Under the applied voltage of 2v, the duration of colored process and bleaching process of the semisolid - state smart window was 2s and 1. 5s respectively, which denoted rapid response velocities. researches on the glass / ito / wo3 / linbo3 / niox / au all solid - state smart window were referred to the effect of each film ' s thickness on the device ' s electrochromic properties. through the test of the visible light transmittance of the colored state and bleaching state of the device, it proved good electrochromic capabilities with the dynamic optical density changed between 0. 2 - 0. 5
並在此基礎上繼續研究了glass ito wo _ 3 linbo _ 3 nio _ x au結構的全固態智能窗器件模型，對于各薄膜層厚度對于器件電致變色性能的影響做了初步的研究，測試了器件可見光范圍內的著色褪色透射光譜，光密度變化量在0 . 2 0 . 5范圍內，表明器件具有良好的電致變色性能。 -
To find the parameters of preparation and annealing process associated with the best electrochromic properties of these films, following researches and experiments were carried out : to compare the visible light transmittance of the colored state with bleaching state of the electrochromic films which were annealed at different temperatures and for different duration, to count the dynamic optical density change, and to test the i - v relations of these films " electrochromic cycles and their colored / bleaching response time
對經過不同熱處理溫度和不同熱處理持續時間得到的薄膜樣品的著色褪色可見光范圍內透射光譜的比較，計算薄膜動態光密度變化量的大小，測試薄膜著色褪色循環伏-安關系以及薄膜著色褪色響應時間的快慢，尋求到薄膜呈現最佳電致變色性能時所對應的制備參數與熱處理參數。
分享友人