organobentonite 中文意思是什麼
organobentonite
解釋
有機膨潤土-
Since established we have cooperated with zhejiang industry university refinement research station, we have developed yh series such as dispersed organobentonite, new type super fine organic double crossing modified betonies clay
公司成立以來長期與浙江工業大學精細化研究所合作，成功地開發了yh系列易分散型有機膨潤土新型超細有機復配改性膨潤土系列產品。 -
( 2 ) when the content of organobentonite was 3wt %, the intercalation behaviors depended on the chain length of organic modifier in the bentonite and the content of compatilizer
（ 2 ）在有機膨潤土含量為3wt %時，插層的效果決定於有機改性劑烷基鏈的長度和相容劑的用量。 -
Organobentonite is a kind of hydrophobic bentonite which prepared by exchanging inorganic cations in the layer of bentonite with organic cations or compounds. it combines inorganic bentonite ' s excellent dilatability, adsorption and dispersion with huge hydrophobic area, so it has very good affinity for organic substance, has been widely used in all kinds of organic system
有機膨潤土是用有機陽離子或有機化合物與膨潤土層間的無機陽離子發生交換而生成的一種疏水親油的膨潤土。由於其既具有無機膨潤土優良的膨脹性、吸附性和分散性，又具有疏水親油性的巨大比表面，與有機物具有很好的親和性和相容性，己被廣泛應用於各種有機體系。 -
Economical and practical organobentonite thickening rheological auxiliary agent have advantages of good thickening, settleability resisted, diversity resisted, anti thixortopy and colloid stability. it is widely use in the business lines of oil paint, printing ink, oil - base filler and gasked cement. quality target
經濟實用型有機膨潤土增稠流變助劑具有良好的增稠性防沉降性分散性觸變性和膠體穩定性廣泛應用於油漆油墨油性膩子及密封膠等行業。 -
Economical and practical organobentonite thickening rheological auxiliary agent
Yh - 808經濟實用型有機膨潤土增稠流變助劑 -
Yh - 808economical and practical organobentonite thickening rheological auxiliary agent organic bentonite yh - 908
Yh - 808經濟實用型有機膨潤土增稠流變助劑 -
According to direct and indirect testing results of organobentonite ' s structure and performance, the project that synthesize new organobentonite with calcium bentonite by replacing a part of conventional modifying agent for caprolactam has been proved reasonable and feasible, the affinity of organobentonie for organic substance was improved, it can be used in variable organic system
通過以上對有機膨潤土結構和性能的直接表徵和間接評價，證明以鈣基膨潤土為原料，用己內酰胺取代部分季銨鹽制備新型有機膨潤土的方案是合理的、可行的，制備的有機膨潤土具有對有機物良好的親和性和相容性，可用於各類有機體系。 -
In this paper, high density polyethylene / bentonite nanocomposites were prepared by simple melt compounding, their structures were demonstrated with x - ray diffraction, ft - ir spectra and dta. it was proved that the molecular chain of pe could be intercalated in layered silicate of organobentonite ， the intercalation nanocomposites were obtained
本文採用簡單熔融插層復合法制備高密度聚乙烯/膨潤土納米復合材料，用x -射線衍射、紅外光譜和差熱分析等手段表徵了復合材料的結構，證實聚乙烯分子鏈確已進入有機膨潤土的硅酸鹽片層間，形成插層型納米復合材料。 -
Moreover, we prepared epoxy / bentonite nanocomposites using conventional organbentonite and quaternary ammonium salt / caprolactam modified organobentonite as harbinger respectively. their mechanical performance were tested. the bend strength and modulus of conventional epoxy / bentonite nanocomposite are 73 % and 52. 4 % higher than those of pure epoxy, while the bend strength and modulus of new epoxy / bentonite nanocomposite are 95. 6 % and 64. 2 % higher than those of pure epoxy
與純環氧樹脂固化物相比，傳統有機膨潤土製備的納米復合材料的彎曲強度和彎曲模量分別提高73和52 . 4 ，而新型有機膨潤土製備的環氧樹脂/膨潤土納米復合材料的彎曲強度和彎曲模量分別提高95 . 6和64 . 2 。 -
It indicated that the color removal of new organobentintes are much higher than that of inorgnganic bentonite, the color removal of the organobentonite prapared by a certain proportion of quaternary ammonium salt and caprolactam is the best, 96. 06 %, it is 11. 86 % higher than that of actived carbon
結果表明，各類新型有機膨潤土對印染廢水的脫色率均遠遠高於無機膨潤土的脫色率，季銨鹽/己內酰胺復合插層有機膨潤土的脫色率最高，達96 . 06 ，比活性炭的脫色率高11 . 86 。