  1. Evaluating effects to parlygorskite organising modification by x - ray, tem, sem, ir, viscidity analysis etc. contrasting organising modification effects of parlygorskite original ore and acidified palygorskite, the result shows wd - 51 modification agent has better modification effect to acidified pargorskite than parlygorskite original ore

    對比了用wd - 51對坡縷石原礦和酸化坡縷石進行有機化改性處理的改性效果，表明wd - 51對酸化坡縷石的改性效果要好。
  2. Environmental mineral fibre mainly points crude minerals like sepiolite and palygorskite species layer - chained magnesian silicate, which have excellent physical - chemical properties and are rare environmental mineral materials in the world nowadays because of the rigor of their form conditions. the single crystals of palygorskite are mostly acicular and fibrous, 30 - 80nm of crystal diameter, and are typical crude nano - rank materials

    環境礦物纖維主要指以海泡石、坡縷石類層鏈狀鎂質硅酸鹽為主的天然礦物，具有優良的物化性能，由於其形成條件苛刻，為世界性稀缺的環境礦物材料，其單晶多為針狀、纖維狀，晶體直徑為30 - 80nm ，屬典型的天然納米級材料。
  3. Study on adsorption capacity of nuclide cs in the zeolite and palygorskite

    沸石及凹凸棒石礦物對核素?的吸附性能研究
  4. Study on the adsorption capacity of zeolite and palygorskite for nuclide cs

    沸石及凹凸棒石礦物對核素銫的吸附性能研究
  5. This paper has summarized the researches on the application of such mineral materials as activated carbon, zeolite, montmorillonite, sepiolite, medical stone, palygorskite, aluminum oxide, sodium hydrate, alumen and nanomaterials as cigarette tip additives to the removal of harmful components in cigarette smoke in the last decades

    摘要總結了近幾十年來包括活性炭、沸石、蒙脫石、海泡石、麥飯石、凹凸棒石、氧化鋁、氫氧化鈉、明礬、納米材料等礦物材料作為卷煙濾嘴添加劑以去除煙氣中有毒有害物質的研究和實驗應用及效果。
  6. 3. the author designs ortho - experimentations of palygorskite acidification and organising modification by adopting propyl alcohol as thinner of wd - 51, and acquires the best craft parameters and craft conditions for gaojiawang palygorskite acidification and acidified palygorskite organising modification, namely : the best craft parameters and craft conditions for gaojiawang palygorskite acidification is : parlygorskite : h2o = 1 : 3, activation time 50 min, activation temperature 96, hydrochloric acid concentration 1. 0 n, parlygorskite granularity - 100mesh ; the best craft parameters and craft conditions for gaojiawang acidified palygorskite organising modification is : wd - 51 concentration 2. 0 % ( wt % ), modification temperature 120, and modification time 60 mins, adopting iso - propyl alcohol as thinner of wd - 51. 4

    設計坡縷石粘土酸化正交實驗和有機化改性正交實驗，取得了高家窪坡縷石粘土酸活化處理和酸化坡縷石用wd - 51進行有機化改性處理的最佳工藝參數和工藝條件，即：高家窪坡縷石酸活化處理的最佳工藝參數和工藝條件為：固液比為1 ： 3 （固體為高家窪坡縷石粘土，液體為去離子水） 、活化時間50min 、活化溫度為96 、鹽酸濃度為1 . 0n 、粒度為- 100目。
  7. Main research contents and achievements of this thesis is as follows : l. this paper carries through particular test and analysis to the basic physical - chemical properties of gaojiawang palygorskite, an environmental mineral fibre, by xay, ir, tem, sem etc. this paper has also discoursed upon the development appliance research status in quo and directions of palygorskite. 2. according to the preceding surface modification research achievements to nonmetal mineral materials, the author combines the self characteristics of palygorskite such as the ratio of length and diameter, typical nano - rank particle diameter, big ratio surface area, well - developed crystal growth imperfection and lattice defect etc. the author also designs organising modification ortho - experimentation of palygorskite by adopting iso - propyl alcohol as thinner of wd - 51 and ndz - 401, and acquires the best craft parameters and craft conditions for gaojiawang palygorskite original ore organising modification, namely : wd - 51 concentration 1. 6 % ( wt % ), modification temperature 120 ?, and modification time 60 mins ; ndz - 401 concentration 2. 0 % ( wt % ), c modification temperature 120, modification time 80 mins

    在前人對非金屬礦物材料表面改性的基礎上，結合環境礦物纖維?坡縷石自身的特點（如：長徑比、典型的納米粒徑、大比表面積、發育的晶體生長缺陷和晶格缺陷等） ，通過對坡縷石有機化改性設計正交試驗，採用（ ch _ 3 ） _ 2choh作為稀釋劑，獲得了採用wd - 51和ndz - 401對高家窪坡縷石原礦進行有機化改性的最佳工藝參數和工藝條件，分別為： wd - 51的濃度為1 . 6 （ wt ） ，改性溫度為120 ，改性時間為60min ； ndz - 401的濃度為2 . 0 （ wt ） ，改性溫度為120 ，改性時間為80min 。
  8. Composition and characterization of palygorskite in guanshan with simulative sr and cs radionuclides adsorpted

    官山凹凸棒石飽和吸附鍶?核素后的結構表徵
  9. The ir - spectrometry analysis results show that chemical combination exists between al - zr coupling agent and fiber - like palygorskite in the modified fiber - like palygorskite and the chemical combination between al - zr coupling agent and phenolic resin is the strongest relative to the other three coupling agents, so al - zr coupling agent can be selected to improve the bonding behavior between fiber - like palygorskite and phenolic resin in the friction material

    紅外光譜分析研究表明：偶聯劑改性坡縷石中，鋁鋯偶聯劑與坡縷石在改性過程中發生了相對強烈的化學鍵合；相對于其它三種偶聯劑，鋁鋯偶聯劑和丁腈改性酚醛樹脂產生的化學鍵合最為強烈，因此可以認為鋁鋯偶聯劑能夠較好地改善摩擦材料中丁腈改性酚醛樹脂和坡縷石纖維界面結合狀況。