photocatalysed 中文意思是什麼
photocatalysed
解釋
光催化的-
When the film is deposited at 450, a kind of square substance exists on the surface of it. it is identified as na0. 23 tio2. experiments has proved that it has a negative effect on the photocatalysed efficiency, but it has no influence on the hydrophilicity
450反應溫度時，薄膜表面會有方塊狀物質生成，經推斷為na _ 2o ? xtio _ 2 ，實驗證明它的存在對薄膜的光催化性能有害，但對親水性沒有影響。 -
With the carrier gas flux rising, the film ' s thickness and the degree of crystallization increase. the band gap decreased little, and the photocatalysed efficiency was enhanced
隨著載氣流量的增加，薄膜的厚度增加，結晶性能提高，光學帶隙變窄，光催化效率增加，親水性沒有明顯變化。 -
The film prepared at low temperature was amorphous tio2 and it ' s photocatalysed efficiency was very low
Apcvd法在較低的基板溫度下制備出的tio _ 2薄膜基本上是非晶態的，光催化效率很低。 -
Excessive or less n2o flux would lead the falling down of photocatalysed efficiency under the uv light irradiation. with the doping of n, the photocatalysed efficiency under visible light irradiation was improved obviously
N _ 2o流量過大和過小都會導致薄膜在紫外光照射下光催化性能下降， n的摻雜可以提高薄膜可見光照射下的光催化性能。 -
With the subtrate temperature ' s increasing, the reaction rate increased, the crystal type was transfered from anatase to rutile, the roughness increased, causing the increase in hydropilicity. when substrates " temperature ranged from 450 ~ 550, the tio2 films were composed with the mixture of rutile and anatase, and the photocatalysed efficiency was the best
隨著基板溫度的升高，反應速度增加，結晶類型由銳鈦礦相逐漸向金紅石相轉變，粗糙度增大，親水性逐漸升高，光催化效率在銳鈦礦和金紅石混合晶型時最佳。 -
In this paper a comprehensive introduction of titanium dioxide film, which was focused on photocatalysis and hydrophilicity, had been given. the research background, the self - clean characteristic and some kinds of preparation methods were discussed. a summary about the factors which affect the photocatalysed efficiency and hydrophilicity was made
論文介紹了tio _ 2薄膜光催化和親水性的研究背景、自清潔特性和原理，比較了各種tio _ 2薄膜的制備技術和方法，並對其光催化和親水性的影響因素進行了總結。