recrystallization annealing 中文意思是什麼

recrystallization annealing 解釋
再結晶退火
  • recrystallization : 析晶
  • annealing : 熱處理
  • n : 1. 【羅馬數字】90〈N＝90000〉。2. 【化學】＝nitrogen. 3. ＝North（ern）。N ＝nuclear 核的：N-waste 核廢料。
  1. Zircaloy - 4 sheet, which was cold - worked followed by recrystallization annealing, exhibits longer lcf life in the rolling direction than that in the transverse direction, and the fact that difference in lcf life between both directions becomes larger as the range of plastic strain becomes lower can be attributed to the texture effect, p - solution treatment deteriorates the alloy ' s lcf property because the treatment lowers the average value of alloy ' s schmid factors, and the subsequent annealing - treatment in a - phase range has a impact on the lcf properties, i. e. the subsequent annealing - treatment at 500 ? for 1. 5h results in better property than that at 750 for 1. 5h, which comes mainly from the fact that the alloy annealled at 500 for 1. 5h has lower amount of the precipitate particles than the alloy annealled at 750 for 1. 5h

    對于冷加工后經再結晶退火處理的zr - 4合金，軋制方向的低周疲勞壽命比橫向要大。隨著_ p的降低，兩個方向的低周疲勞壽命的差別相應增加，這是由於合金中存在織構的緣故。冷加工后經再結晶退火處理的zr - 4合金在固溶處理后，抗疲勞性能明顯降低，這主要是由於固溶處理降低了合金的schmid因子；固溶處理后在相區的退火對疲勞性能有影響，即500 1 . 5h退火的抗疲勞性能要優於750 1 . 5h退火，這主要與500 1 . 5h退火的合金中沉澱相粒子的數量較少有關。
  2. The zn / o ratio, c - axis orented and stress were improved by annealing, and also redusing the defect of zno flim, increasing the size of grain. but too high annealing temperature was adverse to recrystallization of zno thin film

    退火能改善zno薄膜的鋅氧比、 c軸的擇優取向和應力狀態，減少薄膜中的缺陷，使晶粒長大，但是過高的退火溫度不利於zno薄膜的重結晶，使zno薄膜的質量變差。
  3. Recrystallization kinetics of the galvanized strip continuous annealing process with acceleration

    熱鍍鋅原板變速連續退火再結晶動力學
  4. The alloys, which were cold - worked followed by recrystallization annealing, display cyclic softening in the range of low strain because the cyclic stress - strain curve lies below the monotonic stress - strain curve, and show cyclic hardening in the range of high strain because the cyclic stress - strain curve lies above the monotonic stress - strain curve

    在低應變范圍，冷加工后經再結晶退火處理的錯合金的循環應力一應變曲線位於單調拉伸曲線的下方，表現為循環軟化;在高應變范圍則位於單調拉伸曲線的上方，表現為循環硬化。
  5. Recrystallization begins after annealing at 433k for 60 min, and then the vcikers hardness decreases

    Ecap十道次后的組織在433k左右發生再結晶，硬度隨之下降。