The relationship between the holding temperature and the average of the equal - area - circle diameter or the average of the roundness was parabolic
而等溫溫度對最終球化組織的平均等積圓直徑和平均球化度的影響呈拋物線關系。 -
Ill 2, xi ' an university of technology 2. at the same holding temperature, when the holding time increased, the equal - area - circle diameter trended to uniform, and the distribution of the roundness approached to gaussian distribution
2 、相同等溫溫度條件下,改變等溫時間,等積圓直徑的分佈隨時間的延長趨向均勻,晶粒球化度接近於正態分佈。 -
3. at the same holding time, when the holding temperature changed, the number of the long equal - area - circle diameter grain increased, and the average of the equal - area - circle diameter lengthened, the average of the roundness heightened
3 、相同保溫時間條件下,改變等溫溫度,等積圓直徑大的晶粒隨溫度的升高而增加,球狀化程度高的晶粒數增多,平均等積圓直徑和平均球化度同時增大。 -
The average of the equal - area - circle diameter was changed from long to short and then to long, to short at last, as a wave. the average of the roundness was changed from low to high and to low again, as para - curve
平均等積圓直徑由大變小再變大再變小,呈波浪狀變化;而晶粒平均球化度則由小變大再變小,呈拋物線狀。 -
The equal - grain - area - circle diameter and the roundness were defined to scale the form factor and quantified the degree of the grain ' s globalization. metallographic analysis, xrd, tem and edax were expired to observe the evolution of the microstructure, the changing of the phase and the changing of the component
定量測試晶粒的等積圓直徑和球化度等形貌參數,比較形變組織的半固態球化效果,採用金相分析、 xrd 、 tem 、 edax等方法觀測組織演變過程特點,並考察第二相及微區成分的變化。