Bismuth ruthenate and silver were selected as conductor phases and the mixture of calcium oxide - alumina - silicon dioxide ( cao - al _ 2o _ 3 - sio _ 2 ) glass and lead oxide - boron oxide - silicon dioxide ( pbo - b _ 2o _ 3 - sio _ 2 ) glass was selected as inorganic binder phases. it was found that, with the increasing of volume fraction of silver and conductor phase, sheet resistivities descend and there are critical thresholds
實驗發現，隨著功能相百分含量的增加，電阻膜層的方阻值逐漸減小，存在兩個臨界閾值，電阻溫度系數偏向正值;功能相中銀百分含量增加，膜層的方阻值逐漸減小，有一個臨界閾值，電阻溫度系數偏向正值。 -
The average partical size of bismuth ruthenate and pbo - b _ 2o _ 3 - sio _ 2 glass was researched. the smaller bismuth ruthenate partical is, sheet resistivity is lower and temperature coefficient of resistance ( tcr ) is more positive and the refiring change ratio is nearer to zero. the limit size of bismuth ruthenate partical is 0. 56 m
研究了各相粉體平均粒徑對膜層性能的影響，結果表明:釕酸鉍平均粒徑越小，膜層的方阻值越小，電阻溫度系數偏正，重燒變化率越接近零值，球磨工藝的極限平均粒徑為0 . 56 m 。 -
Pbo - b _ 2o _ 3 - sio _ 2 glass reacts with bismuth ruthenate and lead ruthenate is produced as transition layer. the transition layer can make the interface gradually change and the properties of resistors are improved at the same time. based on the study above, the way to get series of pastes was developed
鉛硼硅玻璃粉體平均粒徑對厚膜電阻的性能影響有一極值點，約為1 . 51 m ，在該點處膜層的方阻值最小，電阻溫度系數絕對值最小，重燒變化率最接近零值。