rutile structure 中文意思是什麼
rutile structure
解釋
金紅石結構-
When sno2 wt % was controlled for 10 %, the square resistance of sn - in2o3 was minimum. through the characterization of in2o3 / sno2 nano powders, some conclusions were drawn : sno2 nano powder is rutile structure, and in2o3 and sn - in2o3 nano powders are cubic structure. in2o3 / sno2 nano powders were well dispersing with spherical uniform grain, and the mean grain was 4 - 50 nm
通過對inzo3 / snoz納米粉體表徵，得出inzo3 / snoz納米粒子多呈球形、顆粒均勻、分散性良好、組分均勻、純度較高、平均粒徑在4一50lun左右、比表面積達67一156mz / g ; snoz納米粉為正四面體金紅石結構， inzo3和sn一inzo3納米粉為體心立方結構。 -
The one deposited at 300 substrate temperature owns denser crystallites. during the annealing process, with the increasing of annealing temperature, the crystallites become bigger, and crystalline phase begins to transfer. when the annealing temperature gets to 800, tio2 transfers to rutile structure completely
（ 2 ）常溫下制備的tio _ 2薄膜是無定型的， 300濺射薄膜表面有緻密的晶粒，熱處理溫度升高，晶粒變大，晶相開始轉化， 800退火tio _ 2完全轉化為金紅石結構。 -
Compared with 3 %, the temperature of polymorphic transition between anatase and rutile of 8 % which is the molar quantities of mixed rare earth is a little lower. the calcination temperature is a main reason which influences the structure of phase
摻入鏑的含量8時，銳鈦礦相向金紅石相的轉變溫度與3相比有所降低，所以煅燒溫度是影響產物結構的主要原因。
分享友人