sintering quality 中文意思是什麼
-
In recent years at iron - making plant of pangang, the coke ratio of pig iron has reduced evidently by insisting on “ burden preparation ” course, improving quality of sinter, raising wind temperature, increasing rich oxygen quantity and injecting abundant pulverized coal into bf. the solid fuel consumption of sinter has been decreased greatly through insisting on using high - quality calces, practising high feed sintering, actualizing many techniques in solving key problems. at the same time, the energy source base management has been strengthened, and energy - saving work has made great progress, profits generated by energy - saving have exceeded a hundred million yuan
近年煉鐵廠通過堅持「精料」方針，改善燒結礦質量，提高風溫，增大富氧，實施大噴煤，使入爐焦比有明顯下降；燒結堅持用好生石灰，推行厚料層燒結，實施多項技術攻關，固體燃耗大幅度下降；同時加強能源基礎管理，節能工作取得長足進步，節能創效益1億元以上。 -
Based on the analysis of the characteristics of the raw mix slurry preparing process in alumina sintering production process, firstly, a mechanism model based on material balance principle was established as the master - rule model for the quality prediction ; secondly, considering the problem that the alkali liquor composition was unstable and its real - time measurement was difficult, a nn ( neural networks ) prediction model for the prediction of the alkali liquor composition was set up and nesting - integrated with the mechanism model ; finally, using the gray theory for the information mining from the errors of the mechanism model, a gm ( 1, 1 ) compensation model was put forward and parallel - connection - integrated with the mechanism model, achieving a raw mix slurry quality prediction model
摘要針對燒結法氧化鋁生產過程中生料漿配料工藝的特點，根據物料平衡的原理建立機理模型，作為生料漿質量預測的主規律模型；針對堿液成分波動大且難以實時檢測的問題，對堿液成分含量建立了神經網路預測模型，並和機理模型進行嵌套集成；利用灰色理論對機理模型的偏差數據進行信息挖掘，建立了gm （ 1 ， 1 ）補償模型，並與機理模型進行並聯集成，獲得生料漿質量預測模型。 -
Ultrafine powder, the high quality ultrafine power has been got. ( 2 ) the perfect rutile has been got with flame fusion method in developed domestic sjz sintering machine, and the technology of crystal growth has been clearly analyzed. in the end the suitable techniche has been got on the basis of systemic study on the conditions of growth
通過對晶體生長中的籽晶方向、氣氛等的作用的大量深入的研究，得出了金紅石晶體焰熔法生長現階段的最佳工藝條件，即籽晶（ 001 ）在氫氧比為1 ： 1的附近，通過加氫進行擴肩，然後在1450加氧退火24hr后就能夠獲得完整透明的金紅石單晶。 -
Exemoo has developed a reputation for excellence in every area of industrial furnace design, construction, and installation. each job whether a small re - brick or the design and construction of a completely new system is individually tailored to the customers specific needs. our engineers are involved in every step of the process and our crews are specially trained to inspect all jobs to ensure the highest level of quality control. exemoo has worked with our french joint venture partner to bring their advanced technology to the products made in our china facility. these products include : double chamber gas or oil quenching vacuum furnace, low pressure vacuum nitriding furnace, high pressure sintering furnace, etc. we have gained iso9001 accreditation with registration number 0205q15647r0s
易西姆公司在吸收法國技術基礎上，在中國實現國際先進的不同類型的真空爐設計與製造，以向中國客戶提供性價比優性能可靠的各種真空爐，並且致力於各種真空爐的銷售設計生產新工藝與新技術的研發，以及自動化生產線設備與工程的總成，在低壓真空滲碳爐真空高壓氣淬爐真空壓力燒結爐，低壓真空滲氮爐，以及真空爐自動化生產線方面，在國內乃至國際上都處于領先地位。 -
Rapid repairing mass for converter ismade of electro baked magnesite and high - quality synthetic sandand manufactured by adding high fluidity recarburizer ( beveloped by ourselves ) as addition agent withspecial technique. lt has the characteristics of well fluidity, well rapid fluidityand rpid sintering etc. it is applied to hot patching of large area before or after the converter as rapping hole patching and other parts for converter
轉爐快速補爐料是以電熔鎂砂和優質合成砂為主要原料，配以自行研製的高流動性的增碳劑為添加劑，以特殊工藝生產製成，具有流動性好、快速燒結等特點，適合於轉爐的前後大面的熱修補及出鋼口等部位的修補 -
In order to make use of labor power, material resources, financial resources, financial resources and natural resources in the panzhihua iron and steel company, to develop the district of high - grade magnetic material and establish magnetic material industry production base in the west region of china, this paper focus on the study of the application technology of hard ferrite pre - sintering material with high - quality
為充分利用攀鋼現有人力、物力、財力及得天獨厚的自然資源優勢，發展地區高檔磁性材料產業，建設中國西部磁性材料產業基地，本文對高檔永磁鐵氧體預燒料制備應用技術進行了研究。永磁鐵氧體特別是高性能永磁鐵氧體材料是當代社會及其發展的基礎功能材料。 -
In the alumina process with sintering, the slurry comes out from the grind with low quality because of lots of uncertainty factors and the delay of composition analysis, the qualified raw mix slurry is commonly gained through arranging
摘要由於燒結法氧化鋁配置生料漿過程中不確定性因素多，成分分析滯后，造成生料漿出磨合格率低，一般需經調配使生料漿質量指標符合工藝要求。 -
Ceramic grain filters ard made of refined pottery clays added with certain modifiers, and processed of grinding, mixing, shaping and high temperature sintering. they do not contain any substances that harmful to people or environment. they are hard and rough in surface, porous inside the structure, and have the advantages of high mechanical strength, large specific surface area and porosity. when used in water treatment, they behave a activated surface property, a great amount of pollutant entrapment, less water head loss in the filter bed, lower consumption of back - flush water, stable in chemical and gbiologic property, and long service life, ceramic grain filters is a new and efficient filter material to increase the water yield, upgrade the water quality, and save chemicals and energy
陶粒濾料是以精製陶土為主要原料，摻加適量改性劑，經粉碎，混練，成型和高溫煅燒而製成的，不含任何對人體和環境有害的物質.其表面堅硬，粗糙，內部疏鬆，多孔，具有機械強度高，比表面積大，孔隙率大的特性.用於水處理中，具有表面性狀好，截污能力強，過濾水頭損失小，反沖洗耗水量低，化學穩定性和生物學穩定性好，使用壽命長的特點.陶粒濾料是一種能增加水產量，提高出水質量，節省藥劑和能耗的新型高效過濾材料 -
Abstract : a formula of sintering furnace charge is of key importance to the technological process of sintering in producing alumina by the methods of mixture combination. the choice of an accurate formula is necessary for gaining a high - quality sinter mixture and a better techni - cal and economic target
文摘:燒結爐料配方，對混聯法生產氧化鋁燒結工藝過程有著十分重要作用，選擇正確的配方，對獲取高質量燒結熟料和較好的技術經濟指標具有十分重要意義。 -
The vc - fe surface composite shows high wear - resistance, it ' s wear - resistance is 4. 20 times as that of chilling respectively. with the content of v increasing, it ' s rigidity and wear - resistance increases continually. more vc grains gained, and well distributed, better wear - resistance the vc - fe surface composite will show. ( 7 ) surface cermet composite was formed by the means of cast - sintering technique, with the help of adding wc grains and the quantity of heat sent out from the reaction v + c vc, the carbide cermet quality percent exceeds 60 %
在重載干滑動摩擦條件下， vc一fe表面復合材料顯示了很高的耐磨性，其相對耐磨性是可淬硬鑄鐵的4 . 2倍:隨著含v量的增加， vc一fe表面復合材料的鑄態硬度和耐磨性不斷提高， vc顆粒越多，分佈越均勻，表面復合材料的耐磨性就愈好。 -
The company iso9001 - 2000 quality system certification, the company specialized research and development of low - power, high - efficiency high - quality vacuum heat treatment furnace and vacuum brazing furnace, vacuum sintering furnace
公司通過iso9001 - 2000質量體系認證，公司專門研製開發低能耗、高效益高品質的真空熱處理爐和真空釬焊爐、真空燒結爐。 -
In order to overcome the influence of the technology factor in active molybdenum - manganese metallization, the formulation, raw material treatment, painting method and sintering process are improved in alumina ceramics metallization, which can raise the technique level, product quality and uniform
摘要針對影響氧化鋁陶瓷活化鉬錳法金屬化的工藝因素，在配方、原料處理、塗敷方式、燒結等方面進行改進，提高工藝水平，保證質量穩定性、一致性。 -
It is made of high quality low - carbon steel with sintering porous bronze as its interlaye, the modified compound of pom as its surface
該產品是以優質低碳鋼板為基體，中間燒結一層多孔青銅層，表面軋制層改性的聚甲醛（ pom ） 。 -
In this paper, a series of experiments are carried out with dlms for nickel - based metal powder materials, and the effect of process parameters in sample quality was investigated and analyzed. the main works are as following : ( 1 ) the effect mechanism of laser in metal powder and the nucleation mechanism are analyzed. ( 2 ) the process parameters that affect the quality of sintering parts are investigated and the way how they affect is clear
本文基於直接激光金屬燒結成形技術，通過對鎳基高溫合金直接激光燒結成形的研究，從工藝角度研究某型號鎳基高溫合金的激光直接燒結成形性能以及工藝參數對燒結製件性能的影響，所完成的工作主要有: （ 1 ）分析材料與激光相互作用的機理及熔池的動態快速凝固過程。 -
In this paper, systemic experiments are performed on the compositions, processes, microstructures and properties of some high quality pm inserts. main procedures such as mixing, compaction, sintering, re - compaction, re - sintering, heat - treatment, properties detection and mould design and so on are included in these experiments
本文對幾種高性能粉末冶金搖臂鑲塊的成分、工藝、組織和性能等進行了系統的實驗研究，包括混粉、初壓、初燒、復壓、復燒、后續熱處理、性能檢測、現場模具設計等。