Copper - nanosized tibi composites were prepared by in - situ process. the microstructure, mechanical and electrical properties, and dry sliding wear behavior and electric sliding wear of cu - nanosized tib _ 2 in - situ composites was investigated ; mostly task as follows : the thermodynamic data for the reactions between b and ti in the molten liquid of copper were analyzed, the copper matrix composites reinforced by in - situ tibi nanoparticles were prepared by reactions of 8263, carbon and titanium in copper - titanium melt, and copper - titanium, copper - boron in alloy melt, respectively, which controlled the reaction temperature, reaction time and solidification process. the rnicrostructure and mechanical and electrical properties of the in - situ composites were investigated by using optics microscope, tem and xrd
本文採用原位反應法制備了cu -納米tib _ 2原位復合材料，在此基礎上分析了原位復合材料的微結構，進行了干滑動摩擦磨損和電接觸滑動磨損實驗，完成的主要工作如下：從熱力學的角度出發，分析了陶瓷tib _ 2顆粒在銅基體中原位生成的熱力學條件，並用電解銅、工業純鈦、 b _ 2o _ 3 、 c （還原劑）以及cu - ti 、 cu - b等合金為原料，通過控制適當的反應溫度、反應時間和快速凝固等工藝手段，制備了cu -納米tib2原位復合材料。 -
Microstructure of the composite layer was analyzed with help of optical microscope, scanning electronic microscope ( sem ), electronic probe microanalysis ( epma ) and x - ray diffraction ( xrd ). the compacting of the billet and the forming mechanism of the carbide reinforcement were studied based on thermodynamics and kinetics of reaction, sintering theory and the result of dta. at the same time, the wear - resistance of the composite layer was studied under condition of dry sliding friction
利用光學顯微鏡、掃描電子顯微鏡、電子探針以及x -射線衍射儀，分析了表面復合層的基體組織結構；運用反應熱力學、動力學、粉末燒結理論和燃燒合成理論，結合差熱分析結果，探討了表面復合層壓坯的燒結緻密化原理和碳化物增強相的形成機理；利用坯塊在真空燒結爐不同溫度下的燒結出來的顯微組織分析，模擬出坯塊的燒結過程中的化學反應過程。 -
This shows that sliding friction is proportional to the reaction between the surface in contact
這說明滑動摩擦力與接觸表面的作用力成正比。 -
Sintering speed increased greatly with the help of great quantity of heat of the molten iron, the great quantity of heat sent out from the carbonizing reaction and a little quantity of liquid, this sintering type is an instantaneous sintering, the sintering compacting can carry completely in a few minutes, the degree of sintering compacting is very high. ( 6 ) the vc - fe surface composite has high rigidity, it ' s rigidity exceeds 60hrc, under condition of dry sliding friction and overloading
鑄造燒結時，過熱鐵水的巨大熱流密度沖擊、粉料壓坯中的碳化反應的放熱以及壓坯中少量液相的產生使壓坯的燒結速度大大提高，此時屬瞬間液相燒結，在十幾分鐘內燒結過程即可完成，可達到很高的緻密化程度。 （ 6 ）鑄態下vc一fe表面復合材料具有很高的硬度，其鑄態硬度） 60hrc 。