The author of this article used orthogonal test design, arranged the test scheme scientifically, selected material carefully, at last yielded an ultrahigh strength cement - based material ( uhscm ), whose compressive strength exceeded 100 mpa, mainly by using 42. 5 ordinary portland cement, superfine aggregate : nano sio2, superplasticizers and so on
本文是在廣泛閱讀國內外有關資料的基礎上，採用正交設計，科學地安排試驗，精心選材，用42 . 5普通硅酸鹽水泥、納米sio _ 2 、高效減水劑等材料，採用常規工藝配製出了一種抗壓強度超過100mpa的高強水泥基復合材料。 -
The author of this article used orthogonal test design, arranged the test scheme scientifically, selected material aboratively, at last yield a ultrahigh strength cement - based material ( uhscm ), whose compressive strength exceeded 120 mpa, mainly by using 625r ordinary portland cement, superfine aggregate - - silica fume, superplasticizers and so on
本文在廣泛閱讀國內外有關資料的基礎上，採用正交設計，科學地安排試驗方案，精心選材，用625r普通硅酸鹽水泥、超細顆粒集料硅灰、高效減水劑等材料，採用常規工藝配製出了一種抗壓強度超過120mpa的超高強水泥基材料。 -
In the study, a new kind inorganic anchoring material was developed, which consisted of special binder and aggregate, the former is made from clinker, blast furnace slag and compound admixture, and the later is superfine sand. effects of the factors such as clinker / slag, binder / sand, solution / binder and constituent of solution on the strength, set - time and contraction of the matrix made from the anchoring material were studied
上述分析研究得出以下結論：新型無機錨固材料具有早強、快硬、高強特點， 10h .抗壓強度可達26 . 5mpa ， 365天強度可達144 . 0mpa ；初凝時間在40min . 3h .之間，且初終凝時間差在15分鐘以內；在保濕條件下具有微膨脹性，膨脹率在0 . 5 %以內。