  1. The process and mechanism of ball bonding were studied in this paper, specifically, intermetallic compounds ( imc ) formation and reliability on copper wire and aluminum alloy pad bonding joint during thermal aging were analyzed in detail

    本文在對銅絲球鍵合工藝和原理研究的基礎上，著重分析了老化過程中銅絲球與鋁合金焊盤鍵合的金屬間化合物生長及可靠性。
  2. A reliability experiment of thermal aging was carried out for the two types of joints, scanning electron microscopy, energy dispersive x - ray spectrometer and micro x - ray diffractomer were adopted to investigate the interfacial evolution behavior of joints, and kinetics model of imc formation was established. the results show that imc growth follows the parabolic law as a function of aging time at certain aging temperature, imc growth is more sensitive to the aging temperature than the aging time, the activation energy of cu - al imc growth is 97. 1kj / mol and the major forming cu - al imc are cual2 and cu9al4, the activation energy of au - al imc growth is 40. 1kj / mol and the main au - al imc are au4al and au5al2, with au2al and aual at the interfacial periphery of joints, the rate of cu - al imc growth is about 1000 times slower than that of au - al imc, and kirkendall voids and cracks are easily appeared during thermal aging in gold ball bonds while voids and cracks are absent in copper ball bonds even after aging at 200 for 2900 hours and 250 for 169 hours

    研究結果表明:金屬間化合物厚度與老化時間的關系符合拋物線法則，金屬間化合物的生長對老化溫度比老化時間更加敏感; cu - al金屬間化合物生長的激活能為97 . 1kj / mol ，老化后金屬間化合物呈層狀分佈，主要相為cual2和cu9al4 ; au - al金屬間化合物生長的激活能為40 . 1kj / mol ，主要相為au4al和au5al2 ，同時在界面周邊區域生成了au2al和aual ;老化過程中cu - al金屬間化合物生長速率比au - al金屬間化合物生長速率小103數量級;金絲球鍵合點200老化96小時出現了明顯的kirkendall空洞和裂紋，但銅絲球鍵合點200老化2900小時和250老化169小時都沒有形成空洞和裂紋。
  3. The sort, material composite, structure properties and conduction mechanisms of eca ( electrical conductive adhesive ) were discussed in this paper. then three types of ega specimens were designed and made, on which temperature cycles test from - 55 ? to + 125 ? and thermal aging at + 125 ? were carried out. changes of the adhesive strength, eca ' s bulk resistance and contact resistance under the environment stress were summarized and a detailed evaluation on these specimens was given

    本文在全面闡述導電膠的分類組成、物理結構、導電機理的基礎上，設計並製作了三批導電膠樣品，通過對樣品進行長時間的- 55 ? ? + 125溫度循環和125高溫存儲試驗，總結了導電膠粘接強度、體電阻和接觸電阻在環境應力下的變化規律，對三類樣品的長期可靠性做出了全面的評價，並結合導電膠電阻率和「穿流閾值」的計算機模擬，給出了提高導電膠可靠性和電導率的建議，介紹了國內外在高電導率高可靠性導電膠研製方面的一些最新進展。
  4. Analysis and choice of electro - thermal aging life models used in oil - paper insulation

    熱老化壽命模型的選擇研究
  5. Forced air circulation oven type thermal accelerated aging testers

    強迫空氣循環箱式熱加速老化試驗機
  6. The crystal structure of the martensite as quenching state, the variation of the structure of the martensite during non - isothermal aging in the martensite and parent state, under successive deformation condition and under thermal cycling condition in the cu - based shape memory alloys are studied by the x - ray diffraction

    摘要運用x -射線衍射分析技術研究了不同成分銅基形狀記憶合金淬火態馬氏體結構、馬氏體狀態非等溫時效過程中結構的變化規律、母相狀態時效和連續變形過程中馬氏體及母相結構的變化規律以及熱循環過程中馬氏體結構的變化情況。
  7. Test method for thermal - aging characteristics of electrical insulating varnishes applied over film - insulated magnet wire

    薄膜絕緣磁性金屬絲用電絕緣清漆的熱老化特性的試驗方法
  8. The experimental study on the thermal aging combustion property of the composite modified double base propellant and its life - time calculation

    改性雙基推進劑熱老化燃燒性能試驗研究與壽命預估
  9. Under different load, when we apply this software to any time, region and cooling way, we can get the hottest spot increment and aging rating. to manufactory, the software means sounder thermal design, which will meet the load, putted forward by user, while to user, the software equal to a master who can help them decide the capacity rating of the transformer, which will fit the load. by using the software, the potential danger and the waste, caused by unfit load choice may be avoided

    研究開發了計算乾式電力變壓器負載能力的計算軟體，可對于各種絕緣結構，各種冷卻方式和任一地區、任一時間下運行的變壓器在不同運行載荷下的最熱點溫升絕緣老化率進行分析和計算，同時利用該軟體製造廠可以依據用戶提出的運行負載量給出相應的熱設計方案，用戶可根據運行負載情況利用軟體計算所需變壓器的額定容量，避免額定容量選擇不當造成隱患和浪費。
  10. During the accelerated thermal aging and ultraviolet radiation aging of pmma which is used as the core materials of fiber in pof, it was found that the relative permittivity of pmma decreased significantly to approximately equal to its square refractive index

    摘要實驗中觀察到用作塑料光纖纖芯材料的純有機玻璃（聚甲基丙烯酸甲酯）在加速熱老化和紫外老化過程中其相對電容率急劇下降至大約等於其折射率的平方，即有機玻璃由極性聚合物變為非極性聚合物（ 「全去偶極子極化」現象） 。
  11. Based on the fast freeze - thaw test, the alkaline resistance test, the water immersion test, the wet thermal exposure test and artificial accelerated aging test, the influence of the corroding environment on the mechanical behavior of fiber reinforced polymer ( frp ) laminates and adhesive was studied

    摘要通過快速凍融試驗、耐堿性試驗、浸水試驗、濕熱暴露試驗、人工加速老化試驗，研究了腐蝕環境對纖維增強復合材料（ frp ）的復合體及粘結劑力學性能的影響。