Life time of mn2 + in nano - zns was measured and was found to be close to that of the bulk materials. therefore the quenching centers quench the exciton but not the mn2 + ion self. 2. the increasing curves are different in film and ethanol colloids because there is diffusion process of quenching centers in colloids
對薄膜樣品的熒光增強曲線的擬合表明，顆粒表面猝滅中心數目隨輻照時間的衰減函數是非e指數形式;同時考慮溶液中猝滅中心通過向顆粒表面的擴散而逐漸耗盡，很好地解釋了溶膠的增強曲線與固體薄膜的增強曲線的不同。 -
Nano - zns : mn2 + dispersed in pvb film has the same enhancement after exposure in solar light. the material has potential on measuring the dosage of uv irradiation of solar light
薄膜樣品在太陽光輻照下同樣有熒光增強行為，預示該樣品可以作為一種紫外輻照劑量的記錄材料。 -
In this thesis, we studied optical properties of eu3 + and mn2 + doped zns nanocrystallites. the new results are as follows : 1. zns : mn2 + ethanol colloids were synthesized and dispersed into pvb film. the luminescence enhancement of mn2 + was observed after ultraviolet irradiation
制備出納米zns : mn2 +乙醇溶膠和pvb薄膜樣品，均觀察到紫外光輻照下的熒光增強現象，增長倍數超過20倍，高於以前的報導，並發現樣品在固體薄膜和溶膠中有不同的熒光增強行為。 -
In order to prolong the lifetime of the phosphor, na2sio3 liquid phase hydrolyzation and atmospheric chemical vapor deposition of teos and o2 is adopted to form coating of silicon dioxide film on the surface of the electroluminescent phosphor zns : cu in this paper for the first time
為了延長材料的使用壽命，本論文首次採用na _ 2sio _ 3液相水解和teos與o _ 2的常壓化學氣相沉積的方法在zns ： cu發光材料的表面包覆sio _ 2膜層。