The function mechanism of homogenizing - dispersing agent in nr / br / sbr was researched
摘要研究了nr / br / sbr三元共混體系中均勻分散劑的作用機理。The particle size can be controlled by adjusting processing conditions such as milling time, rotating speed of milling pan, static pressure between milling pans and milling temperature, etc. average article size of the powder reduced to micrometer scale in relatively short time and a fraction of which even reached nano scale
利用聚丙烯和尼龍6之間約60oc的熔點差,在200oc左右加ippch6復合粉體,可以使pa6保持固體超細粒子狀態, pp則熔融成為連續相,得到了pa6超細粒子均勻分散的ppch6共混體系。The analysis on the test result shows that the temperature distribution in cfst members caused by solar radiation is nonlinear, and the nonlinear character is most evident when center point of concrete gets its lowest temperature. the temperature of the center point is affected by various directions, especially the strong potential. in the side exposed to the sun in the afternoon, apart from the center point, temperature varies laggardly when the point of concrete in the same series is more close to the center
結果表明,日照作用下截面的溫度場為非均勻場,混凝土中心的溫度達到最小值時,截面溫度場的非線性特性最明顯,圓心點的溫度受各個方向溫度的共同作用,更多地受到強勢方向的影響;下午時處在向陽面的各系列,同一系列上混凝土各點溫度變化隨直徑縮小趨緩,越靠近圓心,溫度變化越緩和,對外部環境(包括氣溫與日照)的影響呈滯后現象越明顯;而在下午時處在背陰面的各系列除圓心點外,同一系列上越靠近圓心的混凝土測點,溫度變化越緩和。2. effect of the viscosity ratio, mterfacial adhesion, processing conditions and composition on the dispersing morphology and properties of pp / eoc blends was investigated. low viscosity ratio and high shear rate during processing were found to produce fine and uniform dispersion of eoc in pp matrix, while low viscosity ratio, high interfacial interaction, good fluidity of elastomer and high shear rate in molding process resulted in fibril dispersion, which afford a guide for controlling the morphology of pp / eoc blends
研究了粘度比、界面相互作用、加工條件和共混比例等因素對pp eoc體系分散形態和性能的影響,發現粘度比小和加工過程中剪切強度大有利於彈性體在基體中分散均勻細化;粘度比小、界面相互作用強、彈性體本身的流動性好及成型時受到的剪切應力大,使彈性體相易變形,沿流動方向取向呈纖,闡明了各因素對形態影響的作用機制,這對pp eoc共混物的形態控制具有重要的指導作用。Several kinds of carbon - black were compared. superconductive carbon - black of ideal structure, larger specific surface area and fewer ash were selected as main conductive filler. at the same time, experiments were made on the different formulations, and the methods of mixing were compared. finally, a reasonable processing method, which kept a stable and even conductivity of the plastic product, was confirmed
通過對幾種炭黑性能進行分析,選擇了結構性高、比表面積大及灰份含量少的超導炭黑做為主要導電填料進行配方系列化實驗,又對其共混方法進行比較,選擇合理的工藝路線使產品的電性能均勻穩定。At the same clay content, the properties of acr / mmt / pvc composites were superior to those of pvc and acr, mmt mixture prepared by means of melt mixing. it is because the montmorillonite was dispersed homogeneously in the composites with nano - dimension. the apparent kinetics of the polymerization process was firstly studied by conventional gravimetric methods in this thesis
還現發在蒙脫土加入量相同的情況下,採用復合物進行共混的pvc樹脂,其力學性能要明顯好於採用熔融共混直接制備的聚氯乙烯/蒙脫土復合材料,這主要得益於無機蒙脫土acr復合物中就已經呈納米級分散,其在pvc中的分散狀態要比熔融共混均勻的多。分享友人