lattice constants-
The calculation and study of the crystal cell parameters of nano - cordierite
納米級堇青石晶胞參數的計算與研究Metallothionein - ii, 6. 8kda, purified from the liver of rabbit induced by cadmium, has been crystallized in the space group p6322 using hanging drop vapor diffusion method, with unit cell parameters
金屬硫蛋白懸滴汽相擴散法空間群晶胞參數不對稱單位中圖分類號:Treatment of the spinel limn2o4 with aqueous acid produces - mno2. x - ray diffraction and atomic absorption spectroscopy show that - mno2 with lattice constant of 0. 806nm preserves the structural framework of the limn2o4 and the conversion of limn2o4 to - mno2 results in some contraction of the lattice
利用limn2o4與稀酸作用制得- mno2 ,經xrd 、原子吸收光譜( aas )分析表明- mno2仍然保持了尖晶石的面心立方點陣,晶胞參數0 . 806nm ; limn2o4經過酸處理、鋰離子脫出后晶胞體積發生了收縮。This paper has described relative information of gold depositions genesis and hunting besed on studying characteristic of occurrence and appearance, compositions of trace elements, cell parameters, thermoelectricity, ir spectroscope with pyrite in huang - sha gold depositon of jiangxi. it can be provided important scientific basis for evaluation this deposition and hunting a similar ore point or zone in huang - sha region
通過對江西黃沙金礦床中黃鐵礦的產狀及形態特徵、成分特徵、晶胞參數特徵、熱電性、紅外光譜特徵等礦物學的詳細研究,討論了黃沙礦中蘊藏的金礦成因及找礦信息,為正確評價該礦床和在該區找尋新的金礦點(帶)提供了重要的依據。After being oriented, cutted and polished, the grown crystals was processed into a series of wafers
將晶體進行定向、切割和拋光,加工成晶片,測定了稀土離子的分凝系數、晶體的晶胞參數和折射率。28. 59 a,
,晶胞參數Determination of crystallinity and lattice parameters of synthetic molecular sieve by x - ray diffraction
射線衍射法測定分子篩晶胞參數與結晶度And the measured lattice parameter of the tabular particles was 3. 90a, which is in agreement with the previously reported for srtio3
測得1200下保溫4小時后得到的srtio _ 3片狀晶粒的晶胞參數為3 . 90 (Using the single crystal x - ray diffraction ( scxrd ) method, we got the lattice constant, and found it was more than that of silicon
利用單晶x - ray衍射( scxrd )對czsige單晶的晶胞進行了測試,發現晶胞參數發生了明顯的變化。Results show that the grain size of all samples is below 100nm, and the lattice parameters and grain sizes are dependent on the sintering temperature
結果表明,前驅體的焙燒溫度對樣品的晶型、晶胞參數及晶粒尺寸有很大影響。The template must also show the proper size and aspect ratio, otherwise, the template particles must be stable with the matrix at the desired growth temperature and environment
模板顆粒必須具有和pmn - pt類似的晶體結構和晶胞參數;模板顆粒必須具備足夠大的徑高比。The spinel limn2o4 is synthesized by the citrous acid method. the x - ray diffraction pattern of limn2o4 show that the product is a spinel phase with a = 0. 824nm cubic unit cell
論文首先採用檸檬酸配位法制備尖晶石型limn2o4 , x射線衍射( xrd )證實了產物的結構,晶胞參數a = 0 . 824nm 。The assay system of the biological activity of lymphotoxin was established using l929 cell as the sensitive target, lt international standard as the positive control and crystal violet staining method to detect viable cell after treated with lt. the best relationship between dosage and effect could be got if the cell seeding density in cell plate was 1. 6 0. 1 104 the dosage of amd was lug / ml, and the starting concentration of dilution in the plate of lt standard was 10 iu / ml with two fold dilution. the credibility of the established system was detected with rhtnfp developed by r & d
為確定經上述步驟純化后得到的目的蛋自lt 27的生物活性,本研究以l929細胞為靶細胞、淋巴毒素國際標準品為參照,採用結晶紫染色法檢測經淋巴毒素處理后存活的細胞,對淋巴毒素生物活性測定的細胞接種濃度、淋巴毒素標準品板上稀釋的起始濃度和梯度稀釋的倍數、放線菌素d的使用劑量等進行條件實驗后,建立了人淋巴毒素生物活性測定方法。After bamgal10o17 doped with sr, ca, the cell volume of each doped phosphors is shrunk and the crystal parameter c is decreased
摻雜少量的sr , ca后,所得的熒光粉的晶格參數c變小,晶胞體積也隨之變小。The results show that a certain extent, the other parameters constant, increasing power, increasing scanning speed, small grains become more dense ; the good and bad of metallurgical belt, the cellular crystal thickness and the availability and distribution of inclusions are affected by the parameters
結果表明:在一定范圍內,其它工藝參數不變,增加功率,增大掃描速度,晶粒更趨緻密細小;工藝參數影響冶金結合帶的優劣、胞狀晶區的厚薄以及夾雜物的有無和分佈。By the increasing of temperature, liyco3 - xo4 was further changed into licoo2 and lixco1 - xo, and then licoo2 formed by the reaction of lixco1 - xo with li2o. the reaction that produces licoo2 is almost completely done at 700, although some remaining li2o and li2co3 present as a partially amorphous film dispersed on the surface of licoo2, which can accelerate the growth of licoo2 crystallites. however, when temperature is higher than 850, some of licoo2 begin to decompose into the solid solution phase of liyco2 - yo2 and lixco1 - xo, and damaged its own crystal structure
制備licoo _ 2的合成反應中licoo _ 2的微結構不斷發生變化,隨著焙燒溫度升高, co _ 3o _ 4晶粒逐漸減小, licoo _ 2晶粒和顆粒逐漸長大,晶格內部缺陷減少, licoo _ 2晶格趨于完整,在焙燒溫度為850時licoo _ 2晶粒達到最大值;焙燒溫度低於700 ,晶胞參數a隨著焙燒溫度上升而減小,晶胞參數c隨著焙燒溫度上升而增大;而高於700則晶胞參數基本保持不變。Preliminary studies have been shown that diamond - like carbon ( dlc ) had a great potential as a durable, wear and corrosion - resistant coating for biomedical implants. surprisingly, carbon nitride ( cnx ) has not received much attention recently in the biomedical field, despite its performance comparable to or greater than that of dlc in this study, cnx and dlc coatings were prepared using the standard dc magnetron sputtering at room temperature
本文採用磁控濺射( magnetronsputtering )技術嘗試在單晶si樣品表面沉積制備碳氮薄膜,研究了薄膜的結構特徵、性能與制備工藝參數之間的規律,並考察細胞在碳氮薄膜上的吸附特性隨制備工藝參數的變化機理,並與類金剛石膜在凝血時間、細胞吸附特性等方面做了對比。At the same time, we design microelectrode array cell electrofusion chip ’ s driver circuit according to the parameters. utilizing max038 chip to produce the
同時,我們根據參數要求,設計出了微電極陣列細胞電融合晶元的外圍驅動電路。After processing, the cell parameter, transparency, optical damage threshold of ktp crystal have been measured as well as the distribution coefficient of doped elements. the results showed that, after dopping, the cell parameter and transparency of ktp crystal changed little ; optical damage threshold increased three orders of magnitude than the common flux ktp, meanwhile, optical homogeneity decresed a little
將ktp晶體加工后測試了它們的晶胞參數、透過率、光損傷閾值、摻雜元素分凝系數等,結果表明,經過摻雜的ktp晶體晶胞參數、透過率等基本沒有變化,光學均勻性稍有下降,而激光損傷閾值卻提高了3倍。分享友人