氫脆裂 的英文怎麼說
中文拼音 [qīngcuìliè]
氫脆裂
英文
hydrogen embrittlement crack-
: 36 < kth < 37 mpa / m3 / 2, 42 < kih < 44mpa / m3 / 2, 51 < kc < 52 mpa / m3 / 2 through the sem fractography, it is know that the susceptibility to brittle failure at room temperature is more than below 100 ?. and the susceptibility to brittle failure increase with hydrogen increasing, under the sustained loading, ductile cracking appears. the quantity of brittle cracking is more with crack growth
T44mpa m 『 q , sl lt52mpa in 』 」斷口分析表明,該合金充氫后其室溫時的氫脆敏感性大於100oc時的氫脆敏感性;且隨氫含量升高,氫脆敏感性增加:在恆載荷的作用下,該合金裂二紋開始擴展時顯示的是韌性起裂;隨裂紋增長,試樣脆性斷裂的比例增大。Acoustic-emission techniques have been used to determine the rate of cracking of highstrength steel due to hydrogen embrittlement.
聲發射技術已被用來確定高強鋼因氫脆而開裂的速率。Testing of high - strength steel building elements for resistance to hydrogen - induced brittle fracture and advice on the prevention of such fracture
高強度結構鋼部件耐氫誘導易脆斷裂的特性.用支柱試驗Hydrogen brittle fracture analysis of two specimens in different conditions
兩種零件不同條件下氫脆斷裂分析Copper - hydrogen embrittlement test
銅.氫脆裂試驗Abstract : in this paper, through the hydrogen - filling test for the kovar alloy of austenite under fixed load, the kovar alloy hydrogen brittleness sensitivity is measured its feature on hydrongen brittleness fracture is studied, and the way of solving the fracture of the kovar alloy is put forward
文摘:通過對面心立方奧氏體的可伐合金衡載荷充氫試驗,測試了其氫脆敏感性並研究了氫斷裂特徵,提出了解決可伐合金脆斷的方法。分享友人