  1. The present work indicates the organic nf membranes and the inorganic nf membranes all have shortages, so develop composite nf membranes that have low cost, mechanically strong and thermally / chemically - resistant, easy to cleanout and good performances is a very important task. in this paper, the preparation of inorganic - organic composite nf membranes were presented. this composite comprise a porous sio2 / al2o3 support substrate, the pore diameters of which ranging from 10 to 15 nm, this inorganic support substrate having a polymer membrane which comprises an polyvinyl alcohol ( pva ) or polyamide ( pa ) densely deposited on at least one of the face surfaces thereof, the structural porosity of such pva and pa membrane ranging from 3 to 5 nm

    本論文以開發無機?有機復合納濾膜為出發點，首先在al _ 2o _ 3多孔微濾膜上利用溶膠?凝膠法制備sio _ 2 al _ 2o _ 3無機復合超濾膜作為無機?有機復合納濾膜的基膜；選用聚乙烯醇和聚酰胺為表面功能層材料，分別探討了以羥基丁二酸和磺基水楊酸為混合交聯劑，採用浸塗法制備了聚乙烯醇sio _ 2 ? al _ 2o _ 3復合納濾膜；以均苯二甲酰氯、哌嗪和二胺為單體，採用界面聚合法制備了聚酰胺sio _ 2 ? al _ 2o _ 3復合納濾膜，並對影響膜性能的諸多因素進行系統研究。
  2. The pertinent research work has been carried out as follows : the transparent nano - tio2 films on soda - lime glass substrates were obtained by sol - gel process. the precursor of nano - tio2 film was ti ( oc4h9 ) 4 and the menstruum was c2h5oh. the preparation conditions which were effecting the nano - tio2 quality were researched

    本文主要就納米tio _ 2薄膜的制備、探索用ecr氮等離子納米tio _ 2的摻雜改性等開展了如下的工作：本文採用溶膠?凝膠法，以鈦酸丁醋做前驅體、無水乙醇做溶劑，水解制備溶膠，然後通過提拉法制備納米tio _ 2薄膜。
  3. The limno2 synthesized by sol - gel method was orthorhombic phase and pmnm space group, with farthing impurity of mn2o3 。 the result of sem showed that the size of flake was about 1 ~ 2 m, the thickness of flake was about 50 ~ 100nm. the highest discharge capacity is 170. 7mah / g

    溶膠凝膠法所得limno2材料的xrd結果顯示，該材料為斜方晶系， pmnm空間群，有極少量mn2o3雜質; sem結果顯示其片層尺寸大約在1 ~ 2 m ，厚度大約為50 ~ 100nm 。
  4. Thus, to improve the specific of lithium ion batteries, main effort should be directed toward the synthesis of new positive electrode materials, i. e. various lithiated oxides that could reversibly intercalate one li atom per 3d - metal atom at about 4v versus li

    O 。由於電壓高、價格便宜和對環境友好而成為最有希望的備選材料之一。首次採用了聚丙烯酸paa為鰲合劑，運用溶膠凝膠法，合成了limn 。
  5. This law includes two steps : first step apply the sol - glue system to prepare pure concentrated stannic acid gel

    該法包括兩步：第一步，應用溶膠?凝膠法制備純凈的濃縮錫酸凝膠。
  6. In order to discuss the application of sol - gel in the preparation of biomembrane, the gel membrane of agarose was prepared by sol - gel with acticarbon and agarose as raw material, at the same time, the catalytic activity of immobilized cod based in the membrane was studied

    為探討生物傳感器用膜的制備，採用溶膠-凝膠法，以活性炭微粉和瓊脂糖制備了瓊脂糖凝膠薄膜並研究了薄膜固定cod的催化特性。
  7. In all the methods of catalysts preparation, sol - gel process drying by high temperature decrepitation could achieve the best catalyst

    而在浸漬法和幾種溶膠?凝膠法中，使用溶膠?凝膠法並使用高溫燒爆法乾燥的催化劑取得了最高的產量。
  8. For 2h, the osc and special surface area decreased sharply, meaning a bad thermal stability. the osc and special surface area of the samples prepared by precipitation keep very well after aged, exhibiting a promising thermal resistance. while the samples prepared by dipping method have a much more stable osc at different temperature, that is, they have a good thermal stability

    研究表明，採用溶膠?凝膠法制備的樣品在老化前具有最大的儲氧量和比表面積，但經高溫老化后，其儲氧量急劇下降，表現出很差的抗高溫老化性能；採用沉澱法制備的樣品在老化前後，其儲氧量和比表面積降幅最小，有良好的高溫熱穩定性能；採用浸漬法制備的樣品不管老化與否，其儲氧量並不隨著儲氧溫度的改變而大起大落，表現出較好的熱穩定性。
  9. The distinctive functions of ultrasonic wave on the preparation of ultrafine powder materials are introduced and the ultrasonic wave - sol - gel method is determined in this paper to prepare ultrafine sno2 powder

    在此基礎上，確定了採用超聲波-溶膠-凝膠法制備sno _ 2超細粉體的技術工藝。
  10. It is well known that wo3 is a conductance - type semiconductor gas sensing material, but the research on fish freshness detector with wo3 - based gas sensor to trimethylamine is still at a beginning stage. in this project, the wo3 - based gas sensors to trimethylamine are made, and their gas sensing performance are researched, especially at low temperature, the results are as follows : 1. the nano - sized wo3 powder is prepared by sol - gel method of sodium tungstate and hydrochloric acid, and its microstructure is analyzed by using xrd, sem and tem, for material ’ s microstructure is closely related to gas sensing performance

    本課題制備了wo3材料，並以它為基材，製作了三甲胺氣敏傳感器，研究了其對三甲胺的氣敏性能，尤其是低工作溫度下的氣敏性能，得到結果如下: 1 、本課題以鎢酸鈉和濃鹽酸為反應物，用溶膠凝膠法制備了納米wo3材料，並採用x射線衍射分析儀（ xrd ） ，掃描電鏡（ sem ） ，透射電鏡（ tem ）對該材料進行結構分析和形貌觀察，研究發現材料的微觀結構與氣敏性能緊密相關。
  11. Sol - gel method was used for preparing the nano - tio2 photocatalytic film on general glas slid and ito conductive glass. the spectrum property, surface image, crystlal type, particle size, thickness and other properties of this film were measured by uv - vis, afm, xrd and other apparatus

    採用溶膠-凝膠法在普通玻璃載波片和ito導電玻璃上制備出負載型納米tio _ 2薄膜，並用uv - vis ， afm ， xrd等對納米tio _ 2薄膜的光譜特性、表面形貌、晶型及粒子大小、薄膜厚度等進行了表徵。
  12. It is shown that the liquid phase methods, in which particularly methods of the sol - gel, deposition, micro - lacteous, hydrothermal / solvothermal reaction and hydrolyze, should be mentioned, as the most wildly used method in the present

    指出液相法，尤其是溶膠凝膠法、沉澱法、水解法、微乳液法、水熱溶劑熱法等是目前制備納米金屬氧化物材料最廣泛應用的方法。
  13. In this thesis, we discuss the preparation of nano - sized sno2 powder by using sol - gel method and the powder produced by this way has been analyzed by means of xrd, sem. tem, and so on

    本文採用溶膠-凝膠法制備出sno _ 2納米粉體，用xrd 、 sem 、 tem等手段對其進行結構表徵，並進一步測試其氣敏性能。
  14. Synthesis and modification of layered limno2 via sol - gel process

    2的溶膠凝膠法合成及其改性
  15. The technologies i explored consist of photolithography technology, lift - off lithography process, technology of growing silicon dioxide films using sol - gel coating technique, and fabrication of na + - k + ion - exchanged glass waveguide. in this thesis, the experiment principles were investigated and the experimental results were given and discussed

    本論文中具體研究的工藝內容有：光刻的工藝參數研究；剝離法光刻工藝的研究；用溶膠凝膠法制備二氧化硅膜； na ~ + - k ~ +離子交換玻璃波導的製作。
  16. Tremendous efforts are underway on the lithium manganese oxides which are considered to attractive alternatives in term of cost, abundance and nontoxicity for lithium ion battery. the spinel li4mn5o12 and cation - doped lithium manganese oxides were synthesized by sol - gel method which is considered as a promising method

    本文以立方晶系尖晶石結構的富鋰鋰錳氧化物為主要研究對象，以檸檬酸為配合劑，用溶膠-凝膠法合成了純凈的單相尖晶石li _ 4mn _ 5o _ （ 12 ）以及摻雜產物。
  17. The major results are as follows : ( 1 ) complexing action is fundamental for this method, while the interaction of molecules in gel precursor is important for uniformity. the ideal structure of complex gel is that complex molecules in the gel connecting with each other mainly by chemical bonds

    得出以下結論： （ 1 ）絡合作用是絡合物溶膠凝膠法的基礎，凝膠中分子間的作用方式是影響凝膠中組分均勻性的重要方面，理想的絡合物凝膠結構應該是絡合物分子之間更多的以化學鍵合的形式相聯。
  18. Citric acid, taking the place of hno3, solutes the substance which does not solute in solution, and it acts as the ligand of metallic ionic and the hydrolysis catalyst of si ( oc2h5 ) 4, which reduces the pollution caused by no2 which forms at the decompose process of the hot treatment. by changing the means of calcine of the drier gel, choosing the suitable temperature to burn the gel, the high temperature calcine time is shorted, which solves the question of the long period calcine. so the preparation process of the matrix and composite was finished by using more lower temperature than the traditional solid state reaction and more shorter time than the traditional sol - gel process

    結果使基質和復合物的制備在比傳統的固相反應法低得多的溫度下和比常規的溶膠凝膠法短得多的時間里完成；五、對基質及復合物的干凝膠、粉體和燒結體進行了ir 、 dta 、 xrd 、 seni及交流阻抗譜表徵，研究結果表明：在溶膠向凝膠的轉化過程中同時存在著正硅酸乙酯自身的聚合作用和檸檬酸鹽絡合物之間的聚合作用：干凝膠向產物粉體的轉化在400600c之間進行；基質li 。
  19. The nanoparticle titanium dioxide was prepared with tnb as raw material by the sol - gel process, the effects of the alcohol salt concentration the kind of solvent the water volume hydro1yze temperature. the dried ways of the wet gel and the calcined temperature of the dry gel on the specific surface area. particle size

    本文以鈦酸丁酯為前驅體，利用溶膠?凝膠法制備了納米級的tio _ 2粉體材料，通過正交實驗研究了醇鹽的濃度、溶劑的種類、水含量、水解溫度、乾燥條件和煅燒溫度等工藝條件對納米粒子的比表面積、粒徑大小及分佈、晶相組成等性能的影響。
  20. Preparation and optical properties of ca - modified lead titanate thin films

    溶膠凝膠法制備鈣改性鈦酸鉛鐵電薄膜及其光學性質研究