炭黑補強膠料 的英文怎麼說

中文拼音 [tànhēibǔqiángjiāoliào]
炭黑補強膠料 英文
black-reinforced compound
  • 炭 : 名詞1. （木炭的通稱） charcoal 2. （像炭的東西） sth. resembling charcoal3. [方言] （煤） coal4. （姓氏） a surname
  • 補 : Ⅰ動詞1 （修理; 修補） repair; mend; patch 2 （補充; 補足;填補） fill up; add supplement; supply; ...
  • 強 : 強形容詞（強硬不屈;固執） stubborn; unyielding
  • 膠 : Ⅰ名詞1 （某些具有黏性的物質） glue; gum 2 （橡膠） rubber 3 （姓氏） a surname Ⅱ動詞（用膠粘） st...
  • 料 : 名詞1 （材料; 原料） material; stuff 2 （喂牲口用的穀物） feed; fodder 3 （料器） glassware 4 （...
  • 炭黑 : acetylene black
  • 補強 : reinforce
  1. The thermal - oxidative - ageing property of nanocomposites was higher than that of carbon black reinforced rubber

    納米復合材料的熱氧老化性能也明顯高於炭黑補強膠料的性能。
  2. Mechanical property, thermal - oxidative - ageing property, flame retardancy and dynamic mechanical analysis ( dma ) of nanocomposites have been studied, and a comparison between nanocomposites and carbon black reinforced rubber was made

    研究了納米復合材料的力學性能、熱氧老化性能、阻燃性能和動態粘彈性等，並與炭黑補強膠料的一系列性能進行了比較。
  3. The tear strength of nanocomposites was improved obviously. when the content of layered silicated is 3 parts, the tear strength of nanocomposites was improved 26. 3 % over carbon black reinforced rubber

    納米復合材料的撕裂強度明顯提高，當層狀硅酸鹽用量為3份時，撕裂強度比炭黑補強膠料提高了26 . 3 。
  4. When the content of layered silicates was 20 parts, the flame retardancy of nbr / layered silicates nanocomposites was 1. 21 times of carbon black reinforced rubber which had the same content of carbon black

    當層狀硅酸鹽用量為20份時， nbr /層狀硅酸鹽納米復合材料的阻燃性能是同量炭黑補強膠料的1 . 21倍。
  5. The mechanical property of rubber / layered silicates nanocomposites was improved obviously, and at the same content of fillers, the mechanical property of nanocomposites was higher than that of carbon black reinforced rubber

    橡膠/層狀硅酸鹽納米復合材料的力學性能得到了明顯的提高，在相同填充劑用量下，納米復合材料力學性能明顯高於炭黑補強膠料的力學性能。
  6. The results of comparison showed that when the content of fillers was from 3 to 10 parts, the mechanical property of nbr / layered silicates nanocomposites is higher than that of carbon black reinforced rubber. the tensile strength of nanocomposites was 1. 84 times of carbon black reinforced rubber, and the tear strength was 1. 49 times

    研究結果表明：當層狀硅酸鹽的用量在3 - 10份范圍內時， nbr /層狀硅酸鹽納米復合材料的力學性能遠遠高於同量炭黑補強膠料的力學性能，拉伸強度最高是炭黑補強膠料的1 . 84倍，撕裂強度最高是炭黑補強膠料的1 . 49倍。