焊縫氣孔 的英文怎麼說

中文拼音 [hànféngqìkǒng]
焊縫氣孔 英文
weld porosity
  • 焊 : 動詞（用熔化的金屬修補金屬器物或使金屬工件連接起來） weld; solder
  • 縫 : 縫名詞1. （接合處） seam 2. （縫隙） crack; crevice; fissure; slit
  • 氣 : Ⅰ名詞1 （氣體） gas 2 （空氣） air 3 （氣息） breath 4 （自然界冷熱陰晴等現象） weather 5 （氣味...
  • 氣孔 : [礦物學] blowhole; [植物學] stoma; [動物學] spiracle; pore; stigma; [冶金學] gas hole; gas pocket; [建築] air hole
  1. Close examination of the plug welds showed the existence of herringbone patterns near the slag and voids in welds.

    對塞焊焊縫的詳細檢查表明在焊渣及氣孔附近，焊縫中存在著人字型裂紋。
  2. Thus the fracture likely initiated from fatigue sharpened cracks originating from slag and void in the plug welds.

    因此，斷裂可能是由於從塞焊焊縫內的焊渣和氣孔外形成的尖銳的疲勞裂紋而產生的。
  3. In order to effectively determine the position and distribution of porosities in laser welding sampes with complex structure, a preliminary research was proceeded on the distribtion features of porosities and a formula which can calculate the buried depth of porosities was deduced based on the line profile distribution curve of the flaw position

    為了確定復雜結構激光焊件焊縫中氣孔缺陷的位置和分佈，對氣孔缺陷的分佈特徵進行了研究，推導出氣孔缺陷埋藏深度的計算公式，設計了峰值異常缺陷和斜凹型異常缺陷投影距離自動提取演算法，確定了缺陷在鈦合金激光焊件中的分佈特徵，並通過模擬試件的破壞性試驗對該公式進行了驗證。
  4. Any severe deficiency of welding seams surface like cracks, pores, slags is forbidden

    焊縫表面不得有裂紋，氣孔，夾渣等嚴重缺陷
  5. Abstract : causes for porosity occurrence in welding seams were investigated by means of statistic analysis of the porosity degree of welding seams of the submerged arc weld spiral pipes made with x65 and q235 steels from different works and mating weld materials, and of selecting proper mating material on the basis of different oxygen contents in the base metals

    文摘:通過對不同廠家生產的x65級和q235鋼材與不同的焊接材料相匹配所生產的螺旋埋弧焊管焊縫內的氣孔進行統計分析，並從鋼材中氧含量的多少及其焊接材料匹配的不同，來研究焊縫中氣孔產生的原因。