熱影響區開裂 的英文怎麼說
中文拼音 [rèyǐngxiǎngqūkāiliè]
熱影響區開裂
英文
cracking of heat-affected zone-
7mpa / km in the center of the zone ( 6 ) in the hot dry rock geothermal energy extraction system, after the system start to operate, the normal stress of crack show the pronounced influence depending on the temperature ' s change in a month, there are a marked drop in temperature nearby the injection well, forming a lower stress area, with the heat extraction, the temperature ' s change even gradually, but the temperature descend quickly nearby the production well, forming a new lower stress area
( 6 )高溫巖體地熱開發中,裂縫面法向應力受溫度變化的顯著影響,在系統開始運行的一個月內,注入井附近區域其溫度降低較快,形成低應力區;隨開采時間的延長,其溫度變化逐漸平緩,而生產井附近區域溫度降低加快,逐漸形成新的低應力區。This segregation behavior of sn accords with the mechanism of non - equilibrium segregation. it can be obtained through the theoretical calculations that the critical time of sn non - equilibrium segregation is 124 seconds at 750 and the critical cooling rate is 8 / s when cooling from 1320. it is suggested that controlling the cooling rate during continuous casting to avoid the critical cooling rate ( 8 / s ) and avoiding high stress near the trough temperature ( 750 ) may control the form
通過研究殘留元素sn的偏聚機制及其對o . 15wt . % c鋼熱塑性的影響,對試驗鋼進行脆性預測:建議在該鋼的連鑄過程中彎道矯直溫度盡量避開塑性谷底溫度750 ,二冷區的冷速盡量避開臨界冷卻速率8 / s ,從而可以減少該低碳鋼連鑄坯表面裂紋和橫向裂紋,提高其成材率。The results show that, when the hardfacing process is not appropriate, the thick martensite structure with high carbon content will form in the overheat region of heat affected zone, and the high residual stress occurred, which are the primary causes resulting in crack
結果表明,堆焊工藝制定不當,熱影響區的過熱區形成高碳粗大馬氏體組織及保留了較大的焊接應力,是導致堆焊層開裂的主要原因。
分享友人