Study on the synthesis of corundum - mullite - gahnite multiphase materials by two - step sintering process using kaolinite as raw material showed that impurities introduced by kaolinite mainly increased the liquid amount at high temperature, which can assist sintering of specimen. the experiment results indicated that the samples with lower gahnite content had better sinterability than others. however, if the gahnite content was relative high, the promoting effect on sinterability caused by kaolinite was not significant
採用天然原料高嶺土二步煅燒合成剛玉?莫來石?鋅鋁尖晶石復相材料研究發現:天然原料中帶入的雜質主要是增加液相量,促進高溫下試樣的燒結;當尖晶石含量較低時,試樣在1300保溫2h時,在1600燒后試樣燒結性能相比之下較好;而當鋅鋁尖晶石含量較高時,天然料對試樣的促燒作用不是非常明顯。Study on the synthesis of corundum - mullite - gahnite multiphase materials by one - step sintering process using high purity raw materials showed that the more the content of gahnite in multiphase materials, the high the volume expansion would be introduced in the system, which resulted in the sintering difficulty of the multiphase materials. while the content of gahnite was controlled about 30wt % and the content of mullite was about 70wt %, the densified multiphase materials can be obtained after fired at 1600 or 1700
採用高純原料一步合成剛玉?莫來石?鋅鋁尖晶石復相材料研究表明:復相材料中鋅鋁尖晶石含量越高,則合成鋅鋁尖晶石時產生的體積膨脹越大,燒結性也就越差;當鋅鋁尖晶石含量為30wt ,莫來石含量較高為70wt左右時,在1600或1700燒后都能得到顯微結構較為緻密的復相材料。Bonded abrasive products. alumimium oxide sintered stick
普通磨具.燒結剛玉磨石Bonded abrasive products. alumimium oxide sintered wheel
普通磨具.燒結剛玉砂輪Effects of - al2o3 nano - powder additions on sintering of high purity corundum brick
3納米粉對高純剛玉磚燒結性能的影響This is because nano - silica can accelerate the sintering process and promote the densification of corundum castble
這是由於納米二氧化矽能夠促進剛玉澆注料的燒結,使結構緻密化所致。分享友人