Theoretical analysis and testing results demonstrated that viton, a new substitute of the former plasticizer, could noticeably improve its performances, which has been proved as the important improvements of the mixture. due to the favorable thermochemistry performance, dicyandiamide can act as a good combustion - rate regulator. the addition of antistatic agent can desirably increase the antistatic capability of the mixture, and the testing results showed that the performance of the improved mixture was excellent
理論分析和測試結果均表明了以氟橡膠取代耐水點火藥中原粘合劑將使藥劑的各項性能有明顯的改善,是耐水點火藥改進的重要方面;雙氰胺具有良好的熱化學特性,作為耐水點火藥改進中的燃燒速度調節劑具有很好的調速效果;抗靜電劑的加入,進一步提高了藥劑的抗靜電能力,測試分析表明改進后藥劑的性能更加優異。After looking up a large amount of native and foreign information, the materials used in the experiment were as follows : ptfe base, graphite filler, molybdenum disulfide filler, copper powder filler, carbon fiber and so on. the experimental method is that the formula was designed according to uniform experimental method, the relationship between formula and frictional property was found with spline function and then the representative test points were chosen from fitting curve to make verification test for optimization. the preparative technique of solid lubricant is cold - press sintering method
經過查閱大量國內外文獻資料后確定原料為:聚四氟乙烯樹脂為基體,加入石墨、二硫化鉬、銅粉、碳纖維等填料;試驗方法為:根據均勻試驗方法設計配方,用樣條函數找出配方與摩擦性能的關系,然後在擬合曲線上選取具有代表性的試驗點進行驗證試驗,達到優化的目的;制備工藝:冷壓燒結法制備固體潤滑劑。Made of high - speed mixing polytetrafluoethylene resin and a certain volume of filling agent ( such as carbon fiber, graphite, molybdenum disulfide, glass fiber and bronze powder etc. ) shaped by moulding then through high heat sintering
用聚四氟乙烯樹酯與一定量的填充劑(如:碳纖維、石墨、二硫化組、玻璃纖維、青銅粉等)經高速混合均勻後用模塑成型經高溫燒結製成。
分享友人