  1. The research result indicated that on the condition of the same mortar fluidity, the preventing effects of mineral and superplasticizer compounded on aar are better than that of mineral used singly, the preventing effects of mineral admixture and entraining agent compounded are better than that of mineral admixtures used singly, the preventing effects of mineral and superplasticizer and entraining agent compounded are lower than that of mineral admixture and entraining agent compounded. the research achievement has some guiding sense on the recognition of aar prevention in pumping hpc and the researches of test methods for determining the alkali reactivity of aggregate used in hpc

    研究結果表明：在相同砂漿流動度條件下，減水劑與礦物摻合料復合使用對堿?骨料反應的抑制作用大於礦物摻合料單獨使用的抑制作用；引氣劑與礦物摻合料復合使用對堿?骨料反應的抑制作用優于礦物摻合料單獨使用的抑制作用；減水劑、引氣劑與礦物摻合料三元復合使用對堿?骨料反應的抑制作用小於引氣劑與礦物摻合料二元復合使用的抑制作用。
  2. The compatibility and harmony among workability, mechanical grade and durability are optimized, with the ground of adjusting composition and dosage of fd - 1 ; after analyzing anti - freezing damage mechanism, it is concluded that temperature is main factor, which affects structure and property of concrete. after two processes of temperature - elevation of hydration heat and temperature - descent of cold - environment, there is original damage in concrete and its existence leads to temperature fields, as results in temperature damage on transition phase > aggregate and cement mortar of concrete

    通過對負溫混凝土早期防凍分析研究認為，環境溫度對混凝土的結構形成及其性能的影響十分突出，水泥水化溫升和環境散熱降溫兩個過程導致混凝土結構內部產生不均勻溫度場，對過渡相、水泥砂漿以及骨料都能產生不同程度的溫度損傷，產生內部溫差應力裂紋，初始損傷也是不可避免的。
  3. Cement may be used alone, but the normal use is in mortar or concrete in which the cement is mixed with inert materials known as aggregate

    水泥可以單獨使用，但一般都用在砂漿或混凝土裡，在其中，水泥與被稱之為骨料的惰性物料混合。
  4. In the view o6f micro mechanics and fracture mechanics, the mechanism of crack generation of mass concrete is expatiated, thermal stress on the interface between aggregate and cement paste of concrete and crack forming and developing is analyzed and the disciplinarian crack developing with temperature is given

    本文從微觀力學和斷裂力學的角度，探討了混凝土結構開裂機理，分析了溫變過程中混凝土骨料與水泥砂漿界面上的溫度應力以及界面裂紋的萌生和擴展，給出了裂縫隨溫度變化的擴展規律。
  5. In light of great harm from alkali - aggregate to concrete, the alkali activation of the limestone to be used as the aggregate for the concrete in the construction of zhangfeng reservoir is fully tested with petrographic method, accelerated mortar bar method and autoclave expansion test etc., so as to ensure the durability of the anti - abrasion concrete therein

    摘要堿骨料對混凝土的危害很大，為保證抗沖磨混凝土的耐久性採用巖相法、砂漿棒快速法、壓蒸法等4種方法對陽城下川灰巖進行檢驗，以充分揭示張峰水庫混凝土粗骨料是否存在堿活性。
  6. In meso - level, concrete is taken as a type of three - phase composite material comprising mortar matrix, aggregate and bond between matrix and aggregate

    混凝土在細觀上是一種由骨料、砂漿和粘結面組成的非線性材料。
  7. In the paper, concrete is taken as three phases composites consisting of aggregate matrix and bond between matrix and aggregate on meso - level. using monte - carlo method, the positions of the aggregate structures are generated. mesh is projected on them, different material properties are assigned to the respective elements according to element location in individual phase

    應用蒙特卡羅方法，在平面上隨機地確定骨料的位置，產生出隨機骨料結構，並進行網格自動剖分，根據其空間位置確定各單元所屬的相，分配相應的材料特性給相應的單元，用以代表骨料、砂漿及兩者之間的過渡層。
  8. In the view of the concrete ' s micro construction, it can conclude that the boundary is the weakest. minute crack occurs firstly at the boundary, and then it spread toward the cements, which are produced by thermal stress

    該模型是從混凝土組成的微細觀角度出發，簡化為水泥砂漿包圍骨料的平面問題，微裂紋首先在界面上產生然後向水泥砂漿中延伸。
  9. In this paper, with complete calculation micro - mechanics method, mass concrete was taken as three - phase composites, which consists of mortar matrix, aggregate and bond between matrix and aggregate. with nonlinear finite element method, the simulation of static and dynamic mechanics performance of the uniaxial compress concrete specimen of dongjiang arch dam and simple supported beam specimen of xiao wan arch dam was studied by means of the software of msc. marc. the number of all kinds of mortar matrix was calculated according to grading of aggregate of three graded concrete and walraven function

    本文採用完全細觀計算力學方法，將大體積混凝土在細觀層次上看成是由粗骨料顆粒、硬化水泥砂漿及其二者之間的粘結界面組成的非均質復合材料，採用非線性有限元方法，在對大型商業有限元軟體? msc . marc二次開發的基礎上，對東江拱壩的三級配混凝土軸壓試件、建設中的小灣拱壩三級配混凝土梁試件在靜、動荷載下的力學性能和破壞過程進行了數值模擬。
  10. In the dissertation, the study on carbon fiber reinforced concrete ( cfrc ) and plain concrete has been reviewed

    本文對碳纖維混凝土（粗骨料）和碳纖維水泥砂漿的國內外研究現狀進行了全面的評述。
  11. The failure of concrete is caused by the formation, growth and confluence of crack, then creating the macro cracks in concrete

    研究表明混凝土的開裂，首先起源於骨料和砂漿的粘結界面，進而發展至砂漿中。