緻密相 的英文怎麼說

中文拼音 [zhìmìxiāng]
緻密相 英文
dense phase
  • 密 : Ⅰ名詞1 （秘密） secret 2 [紡織] （密度） density 3 （姓氏） a surname Ⅱ形容詞1 （距離近; 空隙小）...
  • 相 : 相Ⅰ名詞1 （相貌; 外貌） looks; appearance 2 （坐、立等的姿態） bearing; posture 3 [物理學] （相位...
  1. The powder was pressed through molding and cold isostatic pressure, which increased the density and decreased the uneven distribution of stress inside the briquet to make the ceramic briquet equally compact

    粉料採取模壓和冷等靜壓相結合的方法壓制，增大了坯體內部的密度並減少了應力的分佈不均，得到均勻緻密的陶瓷坯體。
  2. Mas precursor powders were uniaxially pressed at 100 mpa employing a lubricated steel cylindrical mold. after sintering at 1450 for 2 hours, single - phase cordierite ceramic is prepared, and its relative density is 95. 1 %

    Mas先驅體粉末在100mpa的軸向壓力下成型后，經1450無壓燒結2小時，得到單相堇青石陶瓷，其緻密度達95 . 1 。
  3. The formation of new phase such as mullite and gahnite by solid - phase reaction in multiphase materials can benefit the sintering of materials at 1700, decreased apparent porosity to less than 5 %. reducing atmosphere inhibited the synthesis of mullite and gahnite, played a negative role in the densification of multiphase materials

    固相反應生成的鋅鋁尖晶石和莫來石具有較高的活性，使復相材料在1700燒后顯示出更好的燒結性能，其顯氣孔率降低到5以下；還原性氣氛阻礙了莫來石和鋅鋁尖晶石的生成，不利於復相材料的燒結和緻密化。
  4. Study on the synthesis of corundum - mullite - gahnite multiphase materials by one - step sintering process using high purity raw materials showed that the more the content of gahnite in multiphase materials, the high the volume expansion would be introduced in the system, which resulted in the sintering difficulty of the multiphase materials. while the content of gahnite was controlled about 30wt % and the content of mullite was about 70wt %, the densified multiphase materials can be obtained after fired at 1600 or 1700

    採用高純原料一步合成剛玉?莫來石?鋅鋁尖晶石復相材料研究表明：復相材料中鋅鋁尖晶石含量越高，則合成鋅鋁尖晶石時產生的體積膨脹越大，燒結性也就越差；當鋅鋁尖晶石含量為30wt ，莫來石含量較高為70wt左右時，在1600或1700燒后都能得到顯微結構較為緻密的復相材料。
  5. Cells with dense ysz films provideopen - circuit voltage ( ocv ) of 1. 08v, which is very close to the ocv predictedby nernst equation

    基於緻密電解質膜的電池開路電壓可以達到1 . 08v ，與根據能斯特方程計算的理論開路電壓相當。
  6. The study conducted research on the following four fields : firstly, the characteristics of the interfacial polymerization system of piperazine aqueous solution / trimesoyl hexane solution were systematically investigated. the results show that at a certain molar ratio between the two monomers, piperazine and trimesoyl, at the two phase interface, a dense functional layer of ultra low pressure, high permeating flux and high salt rejection formed by controlling the time of interfacial polymerization, such as the composite membrane ( i ), the concentration in water phase is 0. 4 %, and 0. 1 % in organic phase, and the polymerization time is 1 minute

    本文主要進行了四個方面的研究，首先系統分析和研究了哌嗪水溶液均苯三甲酰氯正己烷溶液界面聚合體系特徵、界面聚合反應中各影響因素對膜性能的影響等，結果發現，當界面處兩相單體（哌嗪和酰氯）分子摩爾比為某一比值時，通過控制界面聚合時間（有機相處理時間） ，可以形成超低壓高通量高脫鹽的緻密功能層，如復合膜（ ） ，水相濃度為0 . 4 ，有機相濃度為0 . 1 ，聚合時間1min 。
  7. Components, structure and surface morphology of the resulted films were identified by fourier transform infrared ( ftir ) spectroscopy, x - ray diffraction ( xrd ) and scanning electronic microscopy ( sem ). the analyses showed the content of cubic boron nitride in the resultant films on substrates was rather high and crystal particles of c - bn with uniform size, smooth crystal plane and regular shapes ( quadrangle and hexagon ) densely arrayed on the substrate

    傅里葉轉換紅外吸收（ ftir ）光譜儀、 x射線衍射（ xrd ）儀和掃描電鏡（ stm ）的測量結果顯示，基底上的bn膜中立方相含量很高，且晶粒大小均勻、排列緻密，晶形呈規則的四角和六角形。
  8. The chemical compositions of sei films formed on the interfaces of a3000 samples in different electrolytes during the first charging process are mainly li2co3 and lioco2r, but their textures are different. the sei films formed in ec - based electrolytes are thin and compact, which can prevent the solvated lithium ions from cointercalating between two graphene layers of the graphite crystallites effectively, therefore samples a3000 have small irreversible capacities and good compatibilities with this kinds of electrolytes. however, the sei films formed in pc - based electrolytes are thick but defective, which could not effectively prevent solvated lithium ions from intercalation, therefore sample a3000 shows large irreversible capacities in pc - based electrolytes and bad compatibilities with this kind of electrolytes

    A _ （ 3000 ）試樣在六種不同的電解液中，首次充電過程中所形成的sei膜，其化學組分均為碳酸鋰和烷基碳酸鋰，但在ec基電解液中形成的sei膜薄而緻密，可以有效地阻止溶劑化鋰離子插入石墨層間，不可逆容量少，表現出與a _ （ 3000 ）試樣有良好的相容性；在pc基電解液中形成的sei膜厚，且有缺陷，不能有效地阻止溶劑化鋰離子嵌入試樣中石墨微晶的層間，不可逆容量大，與a _ （ 3000 ）試樣的相容性極差。
  9. The substrates can be relatively close and stationary.

    襯底可能是相當緻密的和穩定的。
  10. W - cu composites prepared from the precipitation w - cu powder have higher sintered density, better mechanical and physical property, more homogeneous and finer microstructure than those prepared from w - cu powder by the balling - reduction method. in chapter 5, a combination of homogeneous precipitation and ball - milling process, namely the mechano - thermochemical process was employed to prepare ultra - fine w - cu powder

    其中，球磨w一cu復合粉（ hp一m ）壓坯在1150下燒結30min后，可獲得相對密度大於99 %的幾乎全緻密的超細晶粒w一cu復合材料， w的顆粒度小於0 . 5林m 。
  11. Using diethanolamine as aminating agent and glacial acetic acid as neutralizing agent, aminated epoxy acrylic cationic resin was prepared. the effect of technology of aminated epoxy acrylic resin on properties of eletrodeposition was studied by conductivity meter and electrophoresis apparatus. it was shown that, conductivity firstly decreased, and then increased with aminating temperature increase. in contrast with putting polyacrylic resin into thin acetic acid solution, the more compact film could be achieved by neutralizing polyacylic resin with glacial acetic acid and then add it into water. when neutralizing temperature was enhanced, the speed of electrodepsidon was found to increase, and the film was also more compact. increasing the dn leads to enhanced conductivity and smaller particle size. when dn equaled to 80, the smoothest film could be achieved

    以二乙醇胺為胺化劑、冰醋酸為中和劑，合成了胺化環氧丙烯酸陽離子樹脂.採用電泳儀和電導率儀，研究了胺化環氧丙烯酸樹脂合成工藝對陰極電泳塗料電沉積性的影響.結果表明，隨著胺化溫度的增加，電泳液電導率先下降後上升.將冰醋酸加入樹脂中中和，後用水稀釋，比樹脂在醋酸稀溶液中中和，電沉積性能更好.電沉積速率隨著中和溫度的上升而增加，電沉積膜緻密性相應增加.中和度（ dn ）愈高，電泳液電導率愈大，粒徑越小，而塗膜外觀在中和度為80時達到最佳
  12. Mitochondria and ribosomes are hard to see, and the ribosome are found to adhere on the surface of endoplasmic reticulum ; golgi body and lysosome do not exist, membranous ring emerges at the secondary spermatocyte stage. the organelles change into pre - acrosome vesicles at middle spermatid stage, and finally pre - acrosome forms acrosome. 2

    浙江華溪蟹在生精細胞階段，染色質形態相似，呈不同程度凝集狀，核仁在精原細胞期出現;精細胞階段，染色質分化成纖絲狀和緻密塊狀，部分核質延伸入輻射臂內，整個核呈淺杯狀。
  13. Automatic temperature coutrol can precisely control the crystalization temperature to ensure grain structure, mechanically controlled casting die speed is used to ensure the density of material

    自動溫控系統對結晶溫度實施準確控制以確保晶粒結構（金相）符合要求。機械控制恆定的鑄造結晶速度以保證材質的緻密性。
  14. In this paper, nanosized al2o3 ceramic particles were chose as reinforcing phase. enhanced with ultrasonic wave the particles were covered with copper using method by electroless plating, the copper - matrix composite was developed by hot - press sintering process of the composite powder. the composition, microstructure, hardness, density and dry sliding wear property of the new material have been studied

    研究路線為：選用納米級al _ 2o _ 3陶瓷顆粒作為增強相，在超聲波的環境中用化學鍍的方法完成對納米al _ 2o _ 3陶瓷顆粒表面的金屬銅包覆，採用熱壓燒結成型技術以復合粉末為原料制備成納米al _ 2o _ 3陶瓷顆粒增強銅基復合材料，研究分析復合材料的成分、組織結構、硬度以及緻密度，對試樣進行了干滑動摩擦磨損實驗。
  15. Modern, list nephrite in nephrite between mineralogy and malachite study after the category in the world, some of gentle jade serpentine jade and poor fossil pre - pressing zoisite, similar china only mountain jade bao, called the nephrite too, obviously mix the non - real jade as the real jade

    在現代，國際上把和田玉列入軟玉礦物學和玉石學范疇后，有的把鮑文玉蛇紋石玉和糟化石緻密黝簾石，相似中國獨山玉，也稱為軟玉，顯然把非真玉混為真玉了。
  16. Four different types of connective tissue cells are found out of the basal lamina, hi the first type of connective tissue cells, most of the nuclei are occupied by normal chromatins, but in other three types of connective tissue cells, abnormal chromatins are rich in nuclei

    4 、結締組織細胞與基膜相連，主要有4類。第1類細胞：細胞核中常染色質居多，而其它3類細胞核內異染色質較多。第2類細胞：細胞質內含有許多體積較小的電子緻密顆粒。
  17. Study of wettability of rapidly solidified tin - based solders

    復合鋼管陶瓷層相組成及緻密化的研究
  18. In the different stage, the mo - cu sinter flan behaved different densified mechanism

    在這兩個階段中，材料的緻密化機制各不相同。
  19. Preparation and penetrability of microencapsulated phase change materials

    原位聚合法制備相變材料微膠囊及其緻密性
  20. Microstructure of the composite layer was analyzed with help of optical microscope, scanning electronic microscope ( sem ), electronic probe microanalysis ( epma ) and x - ray diffraction ( xrd ). the compacting of the billet and the forming mechanism of the carbide reinforcement were studied based on thermodynamics and kinetics of reaction, sintering theory and the result of dta. at the same time, the wear - resistance of the composite layer was studied under condition of dry sliding friction

    利用光學顯微鏡、掃描電子顯微鏡、電子探針以及x -射線衍射儀，分析了表面復合層的基體組織結構；運用反應熱力學、動力學、粉末燒結理論和燃燒合成理論，結合差熱分析結果，探討了表面復合層壓坯的燒結緻密化原理和碳化物增強相的形成機理；利用坯塊在真空燒結爐不同溫度下的燒結出來的顯微組織分析，模擬出坯塊的燒結過程中的化學反應過程。