裂紋擴張 的英文怎麼說
中文拼音 [lièwénkuòzhāng]
裂紋擴張
英文
crack extension-
The results revealed that the fatigue degradation of the material includes three stages : micro - crack appearing at initial stage, a long process of crack propagation and fatigue. failure of the material after suffering the extraordinary degradation of stiffness
結果表明,材料的疲勞衰變主要分為3個階段:產生小裂紋的初始階段;損傷累積擴張階段;材料剛度加速退化,疲勞破壞階段。The opening stress and the life of crack growth is calculated and compared with the test results and the experience formula. the feasibility of the newman theory of opening stress used in the high strength steel is validated. then through the slice synthesis method, the three dimension surface crack of the weld joint of cone - cylinder is decomposed into many plane through cracks
本文將基於裂紋閉合現象建立的帶狀屈服模型,用在平面貫穿裂紋中,計算此時的裂紋張開應力和疲勞裂紋擴展壽命,與試驗結果和經驗公式比較,驗證newman裂紋張開應力理論在高強鋼中的可行性;然後,用切片合成法,把潛艇結構凸錐柱結合殼焊縫處的三維表面裂紋分解成平面貫穿裂紋,用帶狀屈服模型的理論來分析平面貫穿裂紋,得到裂紋沿深度方向的擴展速率,進而得到潛艇結構的疲勞壽命。The research work of the thesis include mainly : ( 1 ) observe a phenomenon which the two fracture modes are simultaneously found near crack tip of a four - point - bend specimen when the ratio of m / q is close to 3. 0mm, criteria m / q, when the fracture mode of four - point - bend specimen transits from void - mode to shear - mode. intensely location plastic distortion is observed in the front of crack tip and the macro - fracture of the specimen with the same m / q belongs to shear - mode fracture
本文主要在以下幾個方面取得了一定的進展:通過四點彎試件的斷口和切片試驗,觀察到裂紋尖端同時存在兩種斷裂機制? ?在兩種斷裂模式相互轉化的臨界狀態附近,裂紋前方既有鈍化和延伸區中的空穴形核擴張,又有銳化角前劇烈的集中剪切變形。
分享友人