附加局部應力 的英文怎麼說

中文拼音 [bùjiājúbùyīnglì]
附加局部應力 英文
additional local stress
  • 附 : Ⅰ動詞1 （附帶） attach; add; enclose 2 （靠近） get close to; be near 3 （依從; 依附） agree to; ...
  • 局 : Ⅰ名詞1 （棋盤） chessboard2 （下棋或其他比賽一次叫一局） game; set; innings 3 （形勢; 情況; 處境...
  • 部 : Ⅰ名詞1 （部分; 部位） part; section; division; region 2 （部門; 機關或組織單位的名稱） unit; mini...
  • 應 : 應動詞1 （回答） answer; respond to; echo 2 （滿足要求） comply with; grant 3 （順應; 適應） suit...
  • 力 : Ⅰ名1 （力量; 能力） power; strength; ability; capacity 2 [物理學] （改變物體運動狀態的作用） forc...
  • 附加 : 1 （額外加上） add; attach 2 （附帶的; 額外的） additional; additive; attached; appended; append;...
  1. The welding technology of francis turbine runners is optimized from the view of subsection welding and local heating by numerical simulation. the result shows that welding residual tensile stress appears in the weld and its area nearby, and peak stress appears in the dangerous area of blades after practising quondam welding technology ; welding residual tensile peak stress in the dangerous area of blades can be decreased by welding both ends earlier and then welding middle section later during subsection welding, and decreasing effect on welding residual stress of the subsection welding is related to the weld length of blade outlets and welding direction of each subsection ; decreasing effect on residual stress of the local heating is direct proportional to heating time, heating temperature, heating area, and inversely proportional to cooling area, and welding residual tensile peak stress in the dangerous area is decreasing trend earlier, and then increasing trend later with heated location increased

    本文利用數值模擬手段對轉輪的焊接工藝從分段焊和局部加熱兩個方面進行了優化，結果表明:採用普通工藝焊接時，葉片焊后殘余拉應力出現在焊縫及其附近區域，並且在葉片出水邊的熔合線附近（危險區域）出現了峰值;在採用優化的分段焊時，先焊兩端后焊中間的方法可以降低葉片危險區域的焊接殘余拉應力峰值，降低效果與葉片出水邊焊段長度、焊縫各段的焊接方向有關;局部加熱法降低轉輪危險區域殘余應力的效果主要與加熱時間、加熱溫度以及加熱面積成正比，與冷卻面積成反比，並且危險區域的殘余應力隨加熱區域的增大呈先降低后升高的趨勢。
  2. On basis of numerical simulation, the optimized weling technological has been vadidated and adjusted by plane test, results show that residual stress of both ends welded in advance can be decreased by the interspace welded later, and decreasing effect is the most obvious in the 50mm range of the interspace ; for local heating, it is 60mm from the edge of heated area to decrease residual stress

    通過平板試驗得到了分段焊與局部加熱合理工藝參數，並在此基礎上，對轉輪的焊接殘余應力場進行了調整與控制，使葉片出水邊危險區域附近產生了較大的殘余壓應力，且轉輪整體的殘余應力水平低於轉輪材料屈服極限的三分之一。