aging behavior
解釋
老化特性-
The lcf behavior of a recrystallized zircaloy - 4 plate at room temperature and 400 show that alloy has better lcf property at rt than at 400, and cyclic hardening at 400 which could be attributed to the dynamic strain aging effects. it is noticeable that the hydrided plate has the same cyclic behavior as the above unhydrided sample at room temperature
在400下，合金錶現出與常溫下不同的循環特性，其循環穩定滯后回線出現鋸齒狀波形，且在整個疲勞過摘要程中呈現出一致循環硬化的現象，這主要是因為合金在400下發生動態應變時效效應的結果。 -
A reliability experiment of thermal aging was carried out for the two types of joints, scanning electron microscopy, energy dispersive x - ray spectrometer and micro x - ray diffractomer were adopted to investigate the interfacial evolution behavior of joints, and kinetics model of imc formation was established. the results show that imc growth follows the parabolic law as a function of aging time at certain aging temperature, imc growth is more sensitive to the aging temperature than the aging time, the activation energy of cu - al imc growth is 97. 1kj / mol and the major forming cu - al imc are cual2 and cu9al4, the activation energy of au - al imc growth is 40. 1kj / mol and the main au - al imc are au4al and au5al2, with au2al and aual at the interfacial periphery of joints, the rate of cu - al imc growth is about 1000 times slower than that of au - al imc, and kirkendall voids and cracks are easily appeared during thermal aging in gold ball bonds while voids and cracks are absent in copper ball bonds even after aging at 200 for 2900 hours and 250 for 169 hours
研究結果表明:金屬間化合物厚度與老化時間的關系符合拋物線法則，金屬間化合物的生長對老化溫度比老化時間更加敏感; cu - al金屬間化合物生長的激活能為97 . 1kj / mol ，老化后金屬間化合物呈層狀分佈，主要相為cual2和cu9al4 ; au - al金屬間化合物生長的激活能為40 . 1kj / mol ，主要相為au4al和au5al2 ，同時在界面周邊區域生成了au2al和aual ;老化過程中cu - al金屬間化合物生長速率比au - al金屬間化合物生長速率小103數量級;金絲球鍵合點200老化96小時出現了明顯的kirkendall空洞和裂紋，但銅絲球鍵合點200老化2900小時和250老化169小時都沒有形成空洞和裂紋。 -
Effect of aging treatment on mechanical property and h2s resistant behavior of acicular ferrite pipeline steels
時效處理對針狀鐵素體管線鋼力學性能和抗硫化氫行為的影響 -
Based on the fast freeze - thaw test, the alkaline resistance test, the water immersion test, the wet thermal exposure test and artificial accelerated aging test, the influence of the corroding environment on the mechanical behavior of fiber reinforced polymer ( frp ) laminates and adhesive was studied
摘要通過快速凍融試驗、耐堿性試驗、浸水試驗、濕熱暴露試驗、人工加速老化試驗，研究了腐蝕環境對纖維增強復合材料（ frp ）的復合體及粘結劑力學性能的影響。 -
Due to aging and utilizing condition changing, rc structures are often needed to be strengthened. rc structures wrapped with steel wire meshwork and reinforced by high strength mortar spray is proved to be a new effective reinforced method not only by the similarity of material behavior to objects strengthened, but also its endurance and easy installing
實際工程中的結構物由於使用壽命或使用條件變化等原因，往往需對其進行加固，加固方法是多種多樣的，其中鋼絲網外噴高強砂漿加固混凝土結構不論從所使用材料性能與原結構的相似性，還是從加固的耐久性和方法的方便性等方面來講，均是一種有效的新型加固方法。 -