analyzing crystal 中文意思是什麼
analyzing crystal
解釋
分光晶體-
Through the analyzing the macro - structure to micro - structure, the author considers that retarding mechanism of citric acid is that citric acid and ca in the gypsum form the complexant ion, and hinder the crystallization center of dihydrate crystal bigger ; that of sodium tripolyphosphate is that it combined with ca, hinders the dissolve of hemihydrate. formation and growth of crystallization center ; that of bone glue is the glue - protection and chemical absorption action of active group, which also retards the formation and growth of crystallization center
通過宏觀到微觀的分析，筆者認為，檸檬酸的緩凝作用的原因主要在於檸檬酸與鈣形成絡合離子，影響了二水石膏晶體的晶核長大過程；多聚磷酸鈉與鈣形成某種復鹽，對于石膏晶體的溶解、成核和長大過程均有強烈的阻礙影響；骨膠則在於膠體對半水石膏的包裹和活性基團的化學吸附，使二水石膏晶體的成核和長大困難。 -
Firstly, we analyze the character of nd : yag, bbo and lbo, for nd : yag crystal and select the nd : yag as the gain medium and lbo as doubling - frequency crystal. ln the theory, analyzing the parameter of the gain medium length, the ratio of the pump - and laser - beam waists. based on the above analysis, we design the resonance cavity
首先，我們對增益介質的性質和非線性晶體bbo和lbo的一些性質進行了比較，選取nd ： yag作為增益介質， lbo作為倍頻晶體。理論上分析了激光器設計中的一些參數值，如增益介質長度、模式交疊率、最佳倍頻條件，並根據理論分析結果設計了諧振腔。 -
We have found the best ways to optimize the growth of quality zno films and got highly c - axis oriented zno films. the microstructures of the films were observed by afm. after analyzing the crystal structures, the crystal tropism and the surface conformation flatness, we found the result that the substrate temperature of 400 ? is ideal for silicon substrates, which conforms to the result of the structure analyse. by analyzing the magnetism of zno films, we found that the films appropriately doped with fe, co ions have magnetism at room temperature and their magnetism can be improved by doping other little cu ion, but it is not certain that the content of cu is higher, the film has more magnetism, so it has the best content of cu. moreover, the films which have best crystal structures may not have the best magnetism
我們採用原子力顯微鏡（ afm ）方法觀察薄膜的顯微結構，利用所得的圖象信息對薄膜的晶粒結構、晶粒取向、表面形態平整度等進行分析討論，認為400的襯底溫度對硅襯底薄膜是合適的，與結構分析的結果一致。通過對薄膜磁性能的分析和研究，我們得出一些有意義的結果：適量過渡金屬離子fe 、 co摻雜的zno薄膜，在室溫下具有鐵磁性，而在此基礎上摻入少量的cu離子能改善薄膜的磁性。摻cu量有個最佳值，而且結構最好的薄膜磁性不一定最好。 -
Abstract : while we were analyzing the proposed theory about the crystal growth, we doubted that the interface phase existed in the process of crystal growth. with this, we had looked for a lot of references connected and analyzed them. we find that the interface - phase does exist in the process of crystal growth and takes a critic role. therefore, we divide the interface - phase into three co - relative parts : interface layer, adsorptive layer and transitive layer. base on the above ideal, we demonstrate the role of interface layer, adsorptive layer and transitive layer in the process of crystal growth respectively. furthermore, we proposal the interface - phase model about the crystal growth
文摘:在分析前人的晶體生長理論時，作者認為晶體生長過程中可能存在界面相；在分析各種晶體生長現象后認為，晶體生長過程中界面相是存在的，並起著十分重要的作用；通過分析研究，將晶體生長過程中的界面相劃分為3個有機的組成部分：界面層、吸附層和過渡層；並進一步論述了界面層、吸附層和過渡層在晶體生長過程中的地位與作用；在此基礎上提出了界面相模型。 -
After analyzing the characteristics of the lithium niobate crystal and the principle of electro - optic phase modulation & the coupling of single - mode fiber with optical waveguide, the fabrication of the single - mode lithium niobate bar waveguide and v - groove has been studied, the new project in which the lithium niobate v - groove is used for the coupling of the single - mode fiber with optical waveguide is put forward
在分析了鈮酸鋰晶體的相關特性、電光相位調制的基本原理以及單模光纖和光波導的對接耦合以後，研究了單模鈮酸鋰條形波導和鈮酸鋰v型槽的製作工藝，提出了使用鈮酸鋰v型槽實現單模光纖與波導耦合的方案。 -
The feasibility of the multiple photorefractive volume applying to wdm system is demonstrated by analyzing the diffractive properties of the eight holographic gratings superimposed in the linbo3 : fe crystal
通過對10 10 10mm ~ 3塊狀linbo _ 3 : fe晶體中用角度復用技術寫入的8重體光柵的衍射特性分析，證實了光寫入多重體光柵應用於波分復用系統的可行性。 -
According to the raman selection rule and the pl measurement, it is reasonable to evaluate the quality of galnp / algalnp mqw by analyzing the relative intensity ratio of a1p - lo / to. ( 4 ) a new modified random element isodisplacement ( mrei ) model is set up to calculate the dependence between the long - wavelength optical phonon frequencies and the composition of iii - v - type ab1 - xcx mixed crystals. the second neighbor force constants are still assumed to be a linear variation with the composition, but the two first neighbor force constants can be evaluated to be a negative exponent variation with the composition, using the overlapped repulsive potential of the ion crystal combination
通過實驗我們找到了在這些結構參數上生產gainp algainpmqw的較理想的結果； （ 3 ）首次用喇曼（ raman ）散射方法研究了常溫下的gainp algainp多量子阱結構，除了指認出喇曼光譜中各光學聲子模外，還結合樣品光致發光譜的測量結果，分析發現喇曼光譜中alp - lo to的相對強度比可以在一定程度上評定晶體gainp algainpmqw的生長質量； （ 4 ）在修正的隨機元素等位移? mrei模型的基礎上建立了一個新模型，計算了ab _ （ 1 - x ） c _ x型?族半導體混晶的長波長光學聲子模頻率的組分變化關系。 -
First, the frequency - temperature ( f - t ) characteristic of quartz crystal resonator is analyzed. then, the frequency - temperature ( f - t ) characteristic curve of at - cut quartz crystal resonator ( at cut angle : 3 = 0, 1 = 35 6 ) is obtained based on analyzing the christoffel equation describing flexibility sound wave in solids, which serves as the theory basis used for temperature compensated, from which the actual circuit of oscillatory circuit is designed
首先對石英晶體諧振器的頻溫特性進行分析，然後通過求解描述固體中彈性聲波的christoffel方程，得到其在切角3 = 0 ， 1 = 356處也即at切石英晶體諧振器的頻率溫度特性曲線，這是本文進行溫度補償的理論依據。 -
Then the article specifies the control principle of the infrared sensor, the dust warehouse detection, the collision detection, the floating switch, the speedometer, the edge - walking detection, the keyboard, the liquid crystal display as well as the vacuum motor, the brush motor, the driver motor and etc. in the software design aspect, through analyzing the link between the bottom hardware and path coverage planning algorithm, it actualizes pid adjustment algorithm for the robot ’ s straight walking, the coordinate transformation and computation of speedometer ’ s return value, providing the basis for the route coverage algorithm
然後，詳細說明了紅外傳感器，塵倉檢測，碰撞檢測，浮動開關，里程計，貼邊行走檢測、鍵盤、液晶顯示以及吸塵電機、毛刷電機、主動輪驅動電機等控制原理。在軟體設計方面，通過分析底層與路徑規劃演算法的銜接，實現了機器人直行pid校正演算法、里程計返回值的坐標變換及計算等演算法，為路徑覆蓋演算法提供依據。 -
In this paper ， first, the author drew some important conclusions by analyzing several technical factors and experimental conditions which would have great influence on the quality of diamond thin films during mpcvd process ， including gas proportion ， the power of microwave ， the plasma ' s location, the nucleation technique, etc. finally ， the author has successfully deposited nanocrystalline diamond thin films with 300nm crystal particles on the slick surface of silicon by using ch4 / h2 gases in the mpcvd system ， and the nanocrystalline diamond thin films was proved to have good field emission performance. all these researches will make the foundation for the field emission cathode of diamond films
本論文中，作者分析了mpcvd方法中氣源成分比、微波功率、等離子體球的位置、成核技術等各種工藝條件對金剛石薄膜質量的影響，並總結得到了一些有意義的結論；同時，在自行研製的mpcvd沉積系統上，於4 - 7kpa 、 1000左右的熱力學條件下，採用ch4 / h2氣源氣氛在光滑的硅襯底上制備出了晶粒尺寸在300納米以下的納米晶金剛石薄膜，測試得到了較好的薄膜場致電子發射性能，為金剛石薄膜場致發射冷陰極的研究工作打下了實驗基礎。 -
Through analyzing for requirement of shell strength and various hardeners, good economical benefit has been achieved by using technology of nh4cl and alcl3 crystal mixed hardener with the same binder and refractory staff
通過對型殼強度性能的要求與不同硬化劑的分析，在粘結劑和耐火材料不變的情況下，應用氯化銨與結晶氯化鋁混合硬化工藝，取得較好的經濟效果。 -
By analyzing the difference on ( loo ) and ( 110 ) face in the structure of dkdp crystal, the different of uv - vis transmission spectra and the different of concentrations of metal impurities in different part of dkdp crystal was explained
通過分析dkdp晶體的原子結構以及柱面和錐面的原子結構差別，解釋了晶體柱面和錐面雜質金屬離子含量差別的原因以及其與紫外可見透過光譜的關系。 -
Results show that zro2 - ni cermet has clear crystalline interface and uniform distribution. its crystal size is 0. 3 p m. through analyzing the data of specific heat of zro2 - ni cermet, it reveals that adulterating cobalt can enhance the wetting quality of ni and zro2
用xrd 、 sem研究了zro _ 2 - ni - co金屬陶瓷的相結構和形貌，確定了合適的燒結溫度，結果表明，材料的晶粒大小和分佈十分均勻，晶界清晰，粒度在0 . 3 m左右。 -
By analyzing the influence of iodide on photoelectron lifetime, the optimization iodide level and doping position that can increase photoelectron lifetime for agcl and agbr emulsion of different crystal structure is obtained
通過對碘化物摻雜作為缺陷電子陷阱對光電子壽命影響的研究，對于不同晶體結構的鹵化銀乳劑得到了能使光電子壽命達到最大的優化摻雜條件。