artificial aging 中文意思是什麼

artificial aging 解釋
人工陳化
  • artificial : adj 1 人工的，人造的；人為的 （opp natural）。2 摹擬的 （opp genuine real）; 不自然的，矯揉造作的...
  • aging : n. 1. 陳釀。2. 熟化。
  1. 90 % uv below 400nm could be shielded by the nano - sio2 sol. the time of the artificial aging of nano - sio2 - modified coatings prepared by the way of in - situ dispersion method was about twice as long as that of the nano - sio2 - modified coatings prepared by dispersing the nano - sio2 powder in the coating directly. on the other hand, the fadeproof time ( reaching the second level of color aberration ) of the nano - sio2 - modified coatings was 1. 83 times as long as that of the national standard for the super coatings

    實驗證明:納米510 :溶膠具有很強的紫外散射屏蔽性能，對400nm以下的紫外光能屏蔽90 %以上;在位分散法納米510 :改性塗料的耐人工老化粉化時間比直接分散法納米510 :改性塗料提高了近1倍，耐變色時間（達到色差2級的時間）是國標優等品要求的1 . 83倍，較相應的未改性塗料提高了約25 % 。
  2. There was an increase in the fadeproof time of 25 percent over the common coatings. both the nano - tio2 - modified coatings prepared by the way of in - situ sythesising method and the nano - sio2 - modified coatings prepared by the way of in - situ dispersion were strong weatherability coatings, which could resist 18 years " weathering if we calculated the result with the standard which argued that 100h of the artificial aging process was equal

    通過原位生成法制備的納米tio :改性塗料和在位分散法制備的納米510 :改性塗料具有超強的耐候性能，以人工老化100h大約相當于室外曝曬一年計算，納米改性的塗料在室外的使用壽命可超過18年。
  3. Standard test method for aging effects of artificial weathering on latex sealants

    人工風蝕對膠乳密封料老化效果的標準試驗方法
  4. Artificial aging factor

    人工老化因素
  5. Artificial aging of inkpad stamp impressions

    印泥印文人為老化的研究
  6. The adhesive specimens shows some degree of deterioration in appearance and mechanical characteristics after artificial aging test

    粘結劑試件在人工加速老化曝露試驗后，其外觀顏色和力學性能均發生一定的變化。
  7. The product has the feature of high elastic, endurance and aging - resistance. every performance index of it is superior to gb14833 - 93 plastic run way national standard, which has passed the inspection of association of china laboratory of artificial synthesis surface layer, track and field

    產品除廣泛適用於體育場館的場地和道路盲道的鋪設外，也是休閑廣場老年公寓青少年活動中心幼兒園豪華辦公室家庭院閣裝置地面鋪裝的最佳選擇材料，深受廣大用戶歡迎。
  8. The product has the feature of high elastic, endurable and aging - resistance. every performance index of it is superior to gb14833 - 93 plastic run way national standard, which has passed through the inspection of association of china laboratory of artificial synthesis surface layer, track and field

    產品除廣泛適用於體育場館的場地和道路盲道的鋪設外，也是休閑廣場老年公寓青少年活動中心幼兒園豪華辦公室家庭院閣裝置地面鋪裝的最佳選擇材料，深受廣大用戶歡迎。
  9. Based on the fast freeze - thaw test, the alkaline resistance test, the water immersion test, the wet thermal exposure test and artificial accelerated aging test, the influence of the corroding environment on the mechanical behavior of fiber reinforced polymer ( frp ) laminates and adhesive was studied

    摘要通過快速凍融試驗、耐堿性試驗、浸水試驗、濕熱暴露試驗、人工加速老化試驗，研究了腐蝕環境對纖維增強復合材料（ frp ）的復合體及粘結劑力學性能的影響。
  10. 3. investigation of heat treatment of the alloy shows the optimal heat treatment parameters is following : solid solution under 47ctc in 1. 5 hours, then water quenched, artificial aging at 120 ?

    三、利用正交方法研究多層噴射沉積a1 ， 22si - 3cu - mg合金的熱處理工藝，得出合金的最佳熱處理工藝為470固溶保溫1 . 5小時，然後在120溫度條件下進行人工時效。
  11. It is used for aging test for wire, cable, the sheath of rubber ( plastics and artificial leather ) and insulation layer, as well as the other high polymer materials under the specific pressure and temperature in the medium of oxygen and compressed air

    本儀器適用於電線、電纜、橡膠（塑料、人造革）護套及絕緣層以及其它高分子材料在規定的壓力和溫度下，在氧氣和壓縮空氣的介質中進行老化試驗。
  12. The common coatings reached first - degree chalking after 1600h of the artificial aging process. the stable nano - sio2 sol was prepared by sol - gel method and the nano - sio2 - modified coatings were prepared by the way of in - situ dispersion method

    用溶膠?凝膠法制備了穩定的納米sio _ 2溶膠，並採用在位分散法制備了納浙江大學碩士學位論文米510 :改性水性丙烯酸酷塗料。