  1. Bismuth ruthenate and silver were selected as conductor phases and the mixture of calcium oxide - alumina - silicon dioxide ( cao - al _ 2o _ 3 - sio _ 2 ) glass and lead oxide - boron oxide - silicon dioxide ( pbo - b _ 2o _ 3 - sio _ 2 ) glass was selected as inorganic binder phases. it was found that, with the increasing of volume fraction of silver and conductor phase, sheet resistivities descend and there are critical thresholds

    實驗發現，隨著功能相百分含量的增加，電阻膜層的方阻值逐漸減小，存在兩個臨界閾值，電阻溫度系數偏向正值;功能相中銀百分含量增加，膜層的方阻值逐漸減小，有一個臨界閾值，電阻溫度系數偏向正值。
  2. For the ceramic materials, the effects of additives such as pbo, b2o3, co2o3, mno2, cr2o3, sb2o3 on the electrical properties of bismuth - free zno - glass varistor were studied. the glass phase formed mainly by pbo and b2o3 during sintering process could decrease the sintering temperature, improve grain uniform growth and inhibit grain second growth. nonlinear property could be improved by properly adding co2o3, mno2, and cr2o3

    對瓷料而言，系統研究了非bi系zno -玻璃料配方體系中pbo 、 b2o3 、 co2o3 、 mno2 、 cr2o3 、 sb2o3等添加劑對壓敏電阻電性能的影響規律，其中， pbo 、 b2o3在燒結過程中形成的玻璃相，可降低燒結溫度，促進晶粒均勻生長，抑制晶粒二次長大， co2o3 、 mno2 、 cr2o3做為非線性添加劑，適量添加可提高樣品的非線性， sb2o3做為改性添加劑，在燒結過程形成的尖晶石相可細化晶粒，抑制晶粒二次生長，改善樣品的綜合電性能。
  3. The average partical size of bismuth ruthenate and pbo - b _ 2o _ 3 - sio _ 2 glass was researched. the smaller bismuth ruthenate partical is, sheet resistivity is lower and temperature coefficient of resistance ( tcr ) is more positive and the refiring change ratio is nearer to zero. the limit size of bismuth ruthenate partical is 0. 56 m

    研究了各相粉體平均粒徑對膜層性能的影響，結果表明:釕酸鉍平均粒徑越小，膜層的方阻值越小，電阻溫度系數偏正，重燒變化率越接近零值，球磨工藝的極限平均粒徑為0 . 56 m 。
  4. Pbo - b _ 2o _ 3 - sio _ 2 glass reacts with bismuth ruthenate and lead ruthenate is produced as transition layer. the transition layer can make the interface gradually change and the properties of resistors are improved at the same time. based on the study above, the way to get series of pastes was developed

    鉛硼硅玻璃粉體平均粒徑對厚膜電阻的性能影響有一極值點，約為1 . 51 m ，在該點處膜層的方阻值最小，電阻溫度系數絕對值最小，重燒變化率最接近零值。