calcium titanate 中文意思是什麼
-
Purpose - to synthesise calcium titanate with a perovkite structure as an anticorrosion pigment for metal protecting paints
目的-採用具鈣鈦礦結構的鈦酸鈣合成用於金屬保護漆的防腐顏料。 -
Nanosized lead titanate ( pt ) and lead titanate doped with calcium and lanthanum ( pclt ) powder obtained by the sol - gel method was added into vinylidene fluoride - trifluoroemylene [ p ( vdf - trfe ) ] to form nanocomposite to be used as the sensing film of the pyroelectric detector. the experiment results show that after mixing in 0. 16 volume fraction of pclt powder, the pyroelectric coefficient of pttp ( vdf - trfe ) composite film was about 37 % higher than that of the pure p ( vdf - trfe ) film prepared under the same condition, and the voltage figure - of - merit of pt / p ( vdf - trfe ) composite film was about 22. 4 % higher
用溶膠-凝膠法制備了鈦酸鉛（ pt ）和摻鈣鈦酸鑭鉛（ pclt ）納米粉粒，與聚偏氟乙烯-三氟乙烯（ p （ vdf - trfe ）均勻復合，由於16的摻鈣鈦酸鑭鉛納米陶瓷粉粒的摻入，使得pclt / p （ vdf - trfe ）復合膜的熱釋電系數值提高了約37 ，探測優值提高了約22 . 4 。 -
Practical implications - calcium titanate can be utilised for the preparation of anticorrosion paints to protect metal bases from corrosion
實際應用-鈦酸鈣可用於制備防腐漆，來保護金屬基板不受腐蝕。 -
Originality / value - the method of synthesising calcium titanate as an anticorrosion pigment is new
新型/價值-採用鈦酸鈣合成防腐顏料的方法乃新型方法。 -
The synthesised calcium titanate was used to prepare epoxy coatings with varying contents of the anticorrosion pigment
合成的鈦酸鈣與不同含量的防腐顏料用於制備環氧樹脂塗料。 -
It was identified that calcium titanate of perovskite structure is a highly efficient anticorrosion pigment for paints
結果發現具鈣鈦礦結構的鈦酸鈣是一種適用於油漆的高效防腐顏料。 -
Findings - calcium titanate was prepared from materials that do not add any impurities to the anticorrosion properties of the pigment
發現-鈦酸鈣由不添加影響顏料防腐性能的任何雜質的材料制得。 -
A 256 elements infrared array was integrated by 3d cmos technology. nanosized lead titanate powder doped with calcium and lanthanum ( pclt ) obtained by sol - gel method was homogeneously mixed with vinylidene fluoride - trifluoroethylene [ p ( vdf - trfe ) ] as the sensing film
用摻鈣和銅的鈦酸鉛（ pclt ）納米粉粒與聚偏氟乙烯一三氟乙烯ip （ vdf trfe ）均勻復合，作面陣的敏感膜。 -
The results were compared with titanium dioxide that served as a starting material for calcium titanate preparation
我們還將結果與用於制備鈦酸鈣的原始料-二氧化鈦進行了比較。 -
Design / methodology / approach - calcium titanate was synthesised from titanium dioxide and calcium carbonate at hight temperature
設計/工藝/步驟鈦酸鈣由二氧化鈦和碳酸鈣在高溫下合成。 -
The literature has not yet described the use of calcium titanate as a pigment with inhibitive properties in paints
至今，沒有文獻資料對鈦酸鈣作為一種具抑制特性的顏料用於油漆進行了相關說明。