  1. In this study we focused on the pinning structure, and prepared [ pt / mn ] n multilayer by dc magnetron sputtering system instead of using co - sputtering, by which we wish to find a way to reduce the critical annealing temperature and shorten the annealing time

    在我們的課題研究中，我們著重對釘扎層進行了研究，工藝上採用了pt / mn多層膜而不是傳統的共濺射的方法。我們希望通過這種方式能夠發現一條降低臨界退火溫度的途徑，並且能夠縮短退火時間。
  2. We prepare the si - sio2 and ge - sio2 thin film by using the dual ion beam co - sputtering method and the rf co - sputtering technique respectively, adjusting the substrate temperature ( ts ) and the annealing temperature ( ta ). then we analysis the structure of the thin film by using the xrd and tem

    論文採用雙離子束濺射和射頻磁控濺射沉積技術，通過改變薄膜沉積過程中基片溫度（ t _ s ）以及薄膜制備完成後退火溫度（ t _ a ）分別制備了si - sio _ 2和ge - sio _ 2薄膜。
  3. Ge - sio2thin films were prepared by an rf co - sputtering technique on p - si substrates from a ge - sio2 composite target. the as - deposited films were annealed in the temperature range of 300 - 1000 under nitrogen ambience. the structure of films was evaluated by x - ray diffraction ( xrd ), x - ray photoernission spectroscopy ( xps )

    當溫度較低時（沉積時的基片溫度ts 450 ，后處理退火溫度ta 800時，制備的樣品均為非晶結構，當溫度較高時（ ts 450 ， ta 800 ）薄膜樣品中才出現si的結晶顆粒。
  4. In this paper, we reported the structural and luminescent properties of si - based oxide films containing semiconductor si, ge or metal al powders prepared by a dual - ion - beam co - sputtering method ( si - sio2 films and al - si - sio2 films ) or rf magnetron sputtering technique ( ge - sio2 films ), and analyze the pl and el mechanism. 1. the composite films of si - sio2 films were prepared by dual ion beam co - sputtering method from a composite target in argon atmosphere

    我們利用雙離子束共濺射和射頻磁控共濺射技術制備了一系列含有半導體si 、 ge顆粒及金屬顆粒al的薄膜，即si - sio _ 2薄膜、 ge - sio _ 2薄膜和al - si - sio _ 2薄膜，分別對它們的結構、光吸收以及發光性質進行了研究。
  5. Study on the fabricating method the fe / al2o3 / fe mtj and co / al2o3 / feni mtj are prepared by ion - beam sputtering systems. the fexcu ( 1 - x ) granule films were evaporated directly using a high vacuum electron beam evaporation. some samples of granule films are annealed at 340c

    用高真空鍍膜機制備了fe _ xcu _ （ （ 1 - x ） ）系列顆粒膜，並對部分膜做了加熱退火處理，樣品被加熱到340並且保溫2小時。
  6. The enterprise deyang sunlight electric co., ltd. has special knowledge within the ranges roasting, thyristor and vacuum coating as well as sputtering

    公司專業從事晶閘管可控硅整流器、烤架以及真空鍍膜和濺射業務。