  1. It can be noticed that both r and t specimens show initial hardening and subsequent softening at the strain amplitude higher than 0. 8 % and cyclic softening from the beginning to fracture under strain amplitude less than 0. 8 % at room temperature, and the cyclic flow stress was always lower in r specimen than in t specimen at the same strain range

    且在相同的應變幅下， t向試樣比r向試樣具有更高的循環流變應力。此外，對r向及t向試樣，低應變幅下呈現出循環軟化現象是因為晶粒旋轉導致循環軟化；而在高應變幅下發生循環硬化是由於孿晶作用的結果。
  2. The experimental results is shown as followings : ( 1 ) the cyclic flow stress - strain curves in an incremental step test could be expressed as the power law relation : ( 2 ) when the strain amplitude is lower during cyclic deformation tests under constant strain control, softening firstly appears, then gradually hardens with the increasing numbers of cycle ; when the strain amplitude is higher, hardening firstly appears, then gradually softens

    試驗結果表明： （ 1 ）循環流變應力與應變的相互關系曲線均符合冪律關系式： （ 2 ）在室溫下進行恆應變幅循環變形過程中，當所控制的應變幅較小時，該材料首先出現循環軟化，之後隨循環周次的增加直至循環失效前該材料出現了硬化現象。當應變幅較大時，該材料開始出現硬化，然後隨循環周次的增加才出現軟化。
  3. The fatigue crack propagation testing of mdyb - 3 pmma material under constant amplitude cyclic loading has been made. the effect of different stress ratios, room temperatures and loading frequencies were investigated in terms of the paris law presentations of the testing results

    本文研究了在恆幅正弦載荷下溫度、頻率和應力比對疲勞裂紋擴展的影響，給出溫度和頻率影響的定性分析，和應力比影響的定量分析，為建立疲勞裂紋擴展模型打下了基礎。
  4. The cycled strain of the alloy is mainly related to the stress amplitude of cyclic loading

    合金的循環應變值主要與合金的循環加載應力幅值有關。