Influenced by the alternating current field, all of the eutectic microstructure of al - 20si - 5fe - ti alloy changed into very small particles which is well - distributed on the base of a - al. electromagnetic stirring stimulates the forming of equiaxed crystal in al - 20si - 5fe - mn alloy. primary iron - phase is transformed from thick needle into smooth block
電磁攪拌促進al - 20si - 5fe - xmn合金中等軸晶的生成，初生富鐵相由原來粗厚的片狀物轉化成比較圓整的塊狀，共晶組織中鐵相主要以較短的針片狀存在。 -
D. nwabunma, t. kyu, “ phase behavior, photopolymerization, and morphology development in mixtures of eutectic nematic liquid crystal and photocurable monomer ”, polymer. 42, 801 ( 2001 )
劉光耀， 「光聚合高分子在微流體管道上的設計與製作」 ，國立成功大學，化學所碩士論文（ 2004 ） -
The eutectic crystal al3fe often is " needle " shape or short line shape but the shape of primary crystal al3fe is relative to the adding amount of fe powder and the temperature of heat preservation stirring. while the adding amount of pure fe powder is few and the temperature of heat preservation stirring is higher than the temperature of liquidus of al - fe binary alloys equilibrium phase diagram, the reaction synthetical primary crystal al3fe exhibits short worm shape
加入量少，保溫攪拌溫度在al - fe二元合金液相線以上，則形成的初晶al _ 3fe呈短蠕蟲狀； fe加入量大，保溫溫度在液相線以上，初晶al _ 3fe以平面方式生長，復合材料中的初晶al _ 3fe呈塊狀或粒狀，尺寸較大（ 10 m以下） 。 -
As one of the semiconductor - metal eutectic material ( sem ), the rod - like eutectic in - situ composite of si & tasi2 has lower work function, excellent electrical transport and the schottky junctions, which was grown - in during the crystal growth step
Si - tasi _ 2共晶自生復合材料作為半導體金屬共晶材料（ sem ）之一，具有較低的功函數、良好的電傳輸特性和自生肖特基結等特點。 -
Used solid - liquid reaction synthesis technology and stirring casting and metal mold chilling processing, al3fe particles and al3fe + al2o3 particles reinforced pure al matrix in - situ composites are fabricated. the metallography analysis shows that the intermetallic al3fe exhibits two kinds of crystalline state - primary crystal al3fe and eutectic crystal al3fe - in al + fe reaction synthetical al matrix in - situ composites
利用固-液反應合成技術和攪拌技術，並結合金屬型激冷鑄造工藝，制備出了al _ 3fe粒子、 al _ 3fe粒子+ al _ 2o _ 3微粒強化的純al基原位復合材料。