ferrite crystal 中文意思是什麼
ferrite crystal
解釋
鐵素體晶體-
Finally build the foundation to prepare the composites of structure and m - type ferrite with structure and function properties. the constituent phases, microstructure and crystal dimension and crystal coalescence, mechanical properties, magnetic properties of the composites were investigated by means of x - ray diffraction ( xrd ), scanning electron micrograp h ( sem ) and transmission electron micrograph ( tem ), mechanical testing instrument, vibrating sample magnetometer ( vsm ) respectively
採用xrd技術鑒定復合材料的物相，利用sem ， tem來分析srfe12o19及其復合材料的結構形貌，顆粒大小及結合情況，使用伺服材料實驗機、洛氏硬度計及振動樣品磁強計（ vsm ）測試了復合陶瓷的抗彎強度、硬度及其磁性能，並探討它們之間關系。 -
The formation process of w - type ferrite underwent from oxide of metal, the m - type transition phase to final w - phase. when the heating rate was 5 / min, at 900 for 3 hrs and 1200 for 4 hrs, pure m - type and w - type ferrites were formed in air respectively. with heat treatment temperature increasing, crystal structure was more intact, the saturation magnetization increased and the coercive force decreased
熱處理過程表明， m型鐵氧體直接由金屬氧化物反應形成，未經歷尖晶石中間相； w型鐵氧體形成由金屬氧化物到m相過渡相最終向w相的轉變；當升溫速率為5 min ，溫度在900 ，保溫3小時和1200保溫4小時，就分別形成單相m相和w相鐵氧體；隨著熱處理溫度的升高和保溫時間的延長，衍射峰變尖銳，結晶更完整，空心微球的飽和磁化強度增大，矯頑力減小。 -
Thinning the crystal grain and increasing the center vent are effective approach to raise the limiting frequency of high permeability mnzn ferrite. through large quantities of experiments, we made progress in raising limiting frequency of high permeability mnzn ferrite. we prepared the broad band mnzn ferrite of which the initial permeability was 10000
通過採用上述實驗中的優化配方、添加劑組合以及制備工藝，我們在高磁導率材料的寬頻特性方面取得了很大的進展，研製出了起始磁導率磁導率為10000的寬頻mnzn鐵氧體材料，當頻率達到300khz時，起始磁導率下降不到20 % ，其性能相當于epcos公司改進的t38材料。